MgB2 thick film grown on Stainless steel substrate with ductility

Qing-rong Feng,Chinping Chen,Ying Lu,Zhang Zia,Jing-pu Guo,Xiao-nan Wang,Meng Zhu,Jun Xu,Yong-zhong Wang

DOI: https://doi.org/10.1117/12.607297

2004-08-27

Abstract:MgB2 thick film was synthesized on the stainless steel substrate by the technique of hybrid physical-chemical vapor deposition (HPCVD), using Mg ingot and B2H6 as the raw materials. The film thickness is about 10 microns. The scanning electron microscope (SEM) images reveal that it is consisting of highly dense MgB2 crystals with the size ranging from 0.2 to 3 microns. The superconducting transition occurs at 38 K (Tc, onset) and ends at 27 K (Tc, zero), giving the transition width of 11 K. The fabricated film exhibits high ductility and remains attached to the substrate after it was bent to a curvature of about 200 microns.

Superconductivity

What problem does this paper attempt to address?

This paper aims to solve the problem of how to grow a thick MgB₂ film with high ductility on a stainless - steel substrate. Specifically, the researchers successfully prepared a thick MgB₂ film with a thickness of about 10 μm on a stainless - steel substrate through the hybrid physical - chemical vapor deposition (HPCVD) technique. The key points of concern in this paper include:

1. **Material selection and preparation method**: Use magnesium ingots and B₂H₆ as raw materials to grow a thick MgB₂ film on a stainless - steel substrate through the HPCVD technique.
2. **Structural characteristics of the film**: It was observed by scanning electron microscopy (SEM) that the prepared film consists of highly dense MgB₂ crystals, and the grain size ranges from 0.2 to 3 μm.
3. **Superconducting properties**: Through resistivity - temperature (ρ - T) measurement, it was found that the superconducting transition of the film starts at 38 K (Tc, onset) and ends at 27 K (Tc, zero), with a transition width of 11 K.
4. **Mechanical properties**: The adhesion between the film and the substrate and its ductility were studied. The results show that even when bent to a radius of curvature of about 200 μm, the film can still be firmly attached to the substrate, showing high ductility.

In conclusion, this study provides an effective method for preparing a thick MgB₂ film, providing a new approach for the manufacture of MgB₂ tapes or wires in low - temperature superconducting applications.