Investigation of Pt-Dy Co-Doping Effects on Isothermal Oxidation Behavior of (Co,ni)-Based Alloy

Lan Hao,Zhang Weigang,Yang Zhigang

DOI: https://doi.org/10.1016/s1002-0721(12)60156-2

IF: 4.632

2012-01-01

Journal of Rare Earths

Abstract:A Co32Ni21Cr8Al0.6Y (wt.%) alloy with and without doping 3 wt.% platinum, or co-doping 3 wt.% platinum and 0.1 wt.% dysprosium was produced by arc melting. The hardness of both base alloy and composition-modified alloy was measured by using a Vickers hardness tester. Isothermal oxidation tests at 1000 °C in static air atmosphere were conducted to assess the isothermal oxidation behavior of the alloys. The microstructure and composition of the tested alloys before and after oxidation were investigated by means of X-ray diffraction (XRD), field emission-scanning electron microscopy (FE-SEM) equipped with energy dispersive spectroscopy (EDS) and back scatter detector. Results showed that platinum had significant influence on microstructure of the tested alloy by the formation of β-(Ni,Pt)Al phase. Addition of 3 wt.% platinum could slightly increase the hardness of the tested alloy. Platinum accelerated phase transformation of alumina from metastable θ-Al2O3 to stable α-Al2O3 and suppressed the consumption of β-phase. Co-doping both 3 wt.% platinum and 0.1 wt.% dysprosium induced the fastest transformation of θ- to α- alumina and the formation of a fine-grained oxide scales. The most effective reduction of oxidation rate was achieved by the Pt-Dy co-doping effects.