Abstract:Mg alloys have poor formability due to their hexagonal tightly packed (HCP) crystal structure, low active shear system at room temperature, and anisotropic behavior in polycrystalline structure. While this situation hindered the development and commercialization of Mg alloys to some extent in the past, today developments in machining, liquid forming and semi-solid forming technology have removed these obstacles. Semi-solid forming of alloys has been the subject of intense R&D since it was discovered in the 1970s. In the semi-solid forming method, it is aimed to obtain ideal microstructure of the alloy, including excellent fluidity, appropriate flow control, adjustable viscosity and controllable grain morphology, thanks to equiaxed spherical solid particles surrounded by liquid. In this study, it is aimed to achieve the spherical microstructure required for the semi-solid shaping of the extruded AZ31 Mg alloy by heating to semi-solid temperatures and isothermal holding in the semi-solid temperature range. To accomplish this objective, rapid heating in the induction coil and controlled holding in the isothermal temperature range were applied to the alloy. Heating the extruded AZ31 Mg alloy to a semi-solid temperature (565-630°C) and subsequently rapid cooling processes lead to many intermetallic Mg17Al12(γ) compounds with heterogeneous distribution both in the equiaxed primary Mg(α) grains and at the grain boundaries as well as a very little eutectic at the grain boundaries. As the semi-solid temperature value increased, the degree of spheroidization increased. However, it was found that the grain growth reached a maximum at one point and there was no significant change in the shape factor as a result of controlled holding time.

Formation of Non-Dendritic Microstructure of Semi-Solid Magnesium Alloy by Introducing Gas Bubbles

Study on Microstructure of Semi-Solid Magnesium Alloy Manufactured by Gas Bubbles Stirring

Microstructure Evolution of Al-Si Semi-Solid Slurry by Gas Bubble Stirring Method

Microstructure and mechanical property of semi-solid magnesium alloy fabricated by twin-screw stirring

Investigation of The Effect of Semi-Solid Temperatures and Holding Times at Isothermal Range On Microstructure of AZ31 Mg Alloy

Influence of Processing Parameters on Microstructure of Casting Rolling Semi-Solid AZ91D Magnesium Alloy

Microstructures of Semi-Solid AZ91D Magnesium Alloys Billets Prepared by Cold Rolling SIMA Method

Microstructure evolution of hot pressed AZ91D alloy chips reheated to semi-solid state

Effects of Heating Temperatures on Microstructure of Semi-solid AZ91D Magnesium Alloy During Partial Remelting

Effective Control of Microstructure Evolution in AZ91D Magnesium Alloy by SiC Nanoparticles in Laser Powder-Bed Fusion

Effect of Rotating Gas Bubble Stirring Process Parameters on Purifying Effectiveness and Mechanical Properties of Sand-Cast Mg–10Gd–3Y–0.5Zr Alloy

Study on Processing Conditions for Semi-Solid Forging of Magnesium Alloys

Microstructure evolution of AZ80 magnesium alloy in semi-solid compression by molecular dynamics simulation

Structure Shape and Forming Mechanism of Semi-Solid Material of AZ91D Magnesium Alloy by SIMA Process

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Study on Semi-Solid Magnesium Alloy Fabricated by Ultrasonic Stirring Method

Semi-Solid Moulding of AZ91D Magnesium Alloy

Microstructure of semi-solid AZ91D magnesium alloy after hot compression

Numerical Simulation and Experimental Validation of Nondendritic Structure Formation in Magnesium Alloy Under Oscillation and Ultrasonic Vibration

Effect of Heating Process on Microstructure of AZ91D Magnesium Alloy During Partial Remelting

Micromechanisms of Medical Mg-Zn alloys during Semi-solid powder forming (SPF)