Effects of electromagnetic stirring and subsequent homogenization treatment on the microstructure and mechanical properties of Al70Zn10Mg10Cu5Si5 multi-component alloy
Jinchuan Wen,Yu Liu,Yuanchun Huang,Yongxing Zhao
DOI: https://doi.org/10.1016/j.jallcom.2023.170725
IF: 6.2
2023-05-01
Journal of Alloys and Compounds
Abstract:Coarse structure and composition segregation inevitably occurred in light-weight multi-component alloys that manufactured by traditional methods due to the high concentration of solute elements. This work proposes a novel idea to address this challenge by using a combination of electromagnetic stirring and homogenization treatment. The optimum ultimate compressive strength and compressive yield strength were 497 MPa and 432 MPa, which were 12.7% and 14.3% higher than those without electromagnetic stirring, respectively. The electromagnetic force increases the number of nuclei and the equiaxed crystal rate by breaking the primary Mg2Si dendrites and shedding the fine grains on the surface of the mold, so as to achieve the purpose of grain refinement. Furthermore, electromagnetic stirring with appropriate frequency can greatly increase the solid solubility, aggravate the lattice distortion, and consequently lead to a noticeable diffusion sluggish effect, resulting in fine and uniform dispersion of the precipitated MgZn2 phase during homogenization. Finally, a strengthening model was established, and the estimated values were highly consistent with the experimental data, with an error ranging within 5%. This study elaborated the microstructure evolution mechanism, offering guidance to fabricate light-weight multi-component alloys with large-size and excellent mechanical properties.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering