Understanding the solute segregation and redistribution behavior in rapidly solidified binary Ti- X alloys fabricated through non-equilibrium laser processing
Zimeng Ye,Kexin Zhao,Zerong Yu,Konda Gokuldoss Prashanth,Fengying Zhang,Yuqi He,Yijie Peng,Wenlu Wu,Hua Tan
DOI: https://doi.org/10.1016/j.addma.2024.104561
IF: 11
2024-11-23
Additive Manufacturing
Abstract:The solute segregation and redistribution during non-equilibrium rapid solidification using laser additive manufacturing (LAM) process directly influence the microstructure morphology and phase distribution, which in turn affects their mechanical properties. In this work, a laser micro-alloying strategy was utilized to preserve the original solidification microstructure in the considered Ti-9Mo, Ti-9Cr, Ti-9Fe, and Ti-9Ni (wt%) alloys. The addition of different β-stabilizing elements (Mo, Cr, Fe, and Ni) resulted in distinct microstructures: Ti-9Mo and Ti-9Cr alloys exhibited larger grains (∼502 μm and ∼733 μm) and cellular morphologies due to minimum constitutional undercooling at the solid-liquid interface. Because of the increased constitutional undercooling, the Ti-9Fe grains are significantly refined (∼398 μm), showing a dendritic morphology with elongated primary dendrite arms. Ti-9Ni exhibited the highest constitutional undercooling, forming equiaxed dendrites. However, due to the significant consumption of solute atoms by the interdendritic eutectic phase Ti 2 Ni, the grains did not further refine (∼396 μm). Combined with the temperature field simulation, the solidification conditions of the alloys were determined. In addition, based on the solute partitioning coefficients ( k ), the different solute redistribution and diffusion behaviors at the solid-liquid interface during the laser micro-alloying process of Ti-9Mo with k > 1 and Ti-9Cr with k < 1 were elucidated, providing essential insights into the formation of typical cellular morphology and enhanced Mo enrichment phenomenon in the Ti-9Mo alloy.
engineering, manufacturing,materials science, multidisciplinary