Abstract:Not only directionally solidified but also refined microstructure was realized in laser melting deposited Nb–Si–Ti alloys.For the DS microstructure, the <100> of NbSS and <110> of (Nb, Ti)3Si tend to be parallel to the LMD building direction.The fracture toughness of the as-deposited sample is up to 20.3 MPa·m1/2.The LMD processing condition resulted in the transformation of fracture mode from cleavage to dimple for NbSS phases.The phenomenon of crack propagation in (Nb, Ti)3Si and crack stopping at NbSS dendrite was observed.Aiming at achieving fine and directionally-solidified microstructure of Nb–Si based alloy, Nb, Si and Ti powder particles were utilized as the raw materials, and laser melting deposition (LMD) experiments were conducted with 1500 W and 2000 W laser power, respectively. The microstructure characteristic, micro-hardness, and indentation fracture toughness were examined by scanning electron microscope (SEM), X-ray energy dispersive spectrometer (XEDS) and X-ray diffraction (XRD). The results showed that the two kinds of as-deposited Nb–17Si–23Ti alloy samples were mainly composed of NbSS, (Nb, Ti)3Si and Ti-rich NbSS, and the microstructure presents rapid directionally-solidified characteristic, in which the <100> crystallographic direction of NbSS and <110> crystallographic direction of (Nb, Ti)3Si tend to be parallel to the LMD building direction. With the laser power increasing from 1500 W to 2000 W, the microstructure became more oriented and homogeneous. For the sample at 2000 W, the dendrite spacing was only about 1–2 μm, and NbSS and (Nb, Ti)3Si couples grow alternately and they are parallel to the building direction strictly. In the meantime the micro-hardness and indentation fracture toughness reached 1075 HV and 20.3 MPa·m1/2, respectively, indicating significant improvement by the directional growth of fine NbSS and (Nb, Ti)3Si phases, and the dimple fracture mode of the NbSS dendrites.<ol class="links-for-figure"><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S1002007120305773-fx1_lrg.jpg">Download : Download high-res image (365KB)</a></li><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S1002007120305773-fx1.jpg">Download : Download full-size image</a></li></ol>

Rapid directionally solidified microstructure characteristic and fracture behaviour of laser melting deposited Nb–Si–Ti alloy

Investigation on the Microstructure and Mechanical Behaviors of a Laser Formed Nb-Ti-Al Alloy

Influence of Laser Power on Microstructure of Nb-16Si Binary Alloys Fabricated by In-situ Additive Manufacturing

In-Situ Tensile Deformation Behavior Of As-Built Laser Direct Metal Deposited Ti-6al-4v Alloy At 200 Degrees C

In-situ Investigation of the Anisotropic Mechanical Properties of Laser Direct Metal Deposition Ti6Al4V Alloy

Microstructures and mechanical properties of Nb nanoparticles modified Ni60 hard-facing alloy fabricated by laser metal deposition

MICROSTRUCTURAL CHARACTERISTICS AND MECHANICAL PROPERTIES OF A Nb/Nb5Si3 BASED COMPOSITE WITH AND WITHOUT DIRECTIONAL SOLIDIFICATION

Phase transformation mechanism and mechanical properties of Ti-45Al-8Nb alloy prepared by directed laser deposition

Unidirectional Crystal Orientation of Dual-Phase Ni3Al-Based Alloy via Laser Irradiation

Microstructure Evolution and Mechanical Properties of a Directionally Solidified Nb-Ti-Si-Cr-Al-Hf-Dy Alloy

Microstructure, Mechanical, and Tribological Properties of Nb-Doped TiAl Alloys Fabricated via Laser Metal Deposition

Effect of Growth Rate on Microstructure and Mechanical Properties in a Directionally Solidified Nb-silicide Base Alloy

Formation Mechanism of Dilute Region and Microstructure Evolution in Laser Solid Forming TA15/Ti2AlNb Dual Alloy

Study of microstructure and compressive strength of a novel Ti-0.75Al-9.5V alloys manufactured by laser deposition melting

Effect of laser scanning speed on microstructure, tribological and corrosion behavior of Ti 23Nb alloys produced by laser metal deposition

Microstructure Evolution and Toughening Mechanism of a Nb-18Si-5HfC Eutectic Alloy Created by Selective Laser Melting

The columnar dendrite and equiaxed dendrite transformation of high Nb-TiAl alloy by laser-directed energy deposition

Microstructure evolution and formation mechanism of a crack-free nickel-based superalloy fabricated by laser engineered net shaping

Microstructures and Mechanical Properties of Laminated Structural Nb-Ti-Al Composites Fabricated by Laser Deposition

Investigation of the Influence of Process Parameters on Crack Formation and Mechanisms in Ti-48Al-2Cr-2Nb Alloy via Laser Directed Energy Deposition

Investigation of macro/microstructure evolution and mechanical properties of directionally solidified high-Nb TiAl-based alloy