Abstract:The processing parameters of a selective laser-melted (SLM) Ti6Al4V alloy were systematically optimized for optimal surface roughness and relative density. The relationship between microstructure and mechanical properties were established in the optimal parameter range. The results showed that the optimal laser power and scan speed was 200-250 W and 850-1150 mm/s, respectively. The laser power and scan speed played contradicting roles in the resultant roughness and porosity. An appropriate increase in laser power and decrease in scan speed could reduce the surface roughness and simultaneously improve the density and dimensional accuracy. When the laser power was 200 W, the microstructure varied from equiaxed grains to mixed equiaxed-columnar grains, and then it varied to columnar grains as the scan speed changed from 250 mm/s to 850-1750 mm/s. The acicular structure inside the grains transformed from an alpha (alpha') + beta phase to an alpha' (alpha) phase with gradual grain refinement. Some nano-beta phase precipitated near the acicular phase. Micro-hardness measurements revealed different values at the top, middle and bottom of the samples with increasing laser power and showed a reduced hardness gap with increasing scan speed. However, the elongation continuously increased with increasing scan speed and reached a maximum value of 7.8% at a scanning speed of 1150 mm/s. Decrease in elongation was observed when the laser power increased to 275 W. These variations in the hardness and mechanical properties were attributed to the combined effects of nano-beta phase and grain refinement of acicular alpha (alpha') martensites.

Prediction of solidification microstructure of titanium aluminum intermetallic alloy by laser surface remelting

Solidification Microstructure Prediction of Ti-6Al-4V Alloy Produced by Laser Melting Deposition

Effects of Processing Parameters on a Β-Solidifying TiAl Alloy Fabricated by Laser-Based Additive Manufacturing

Prediction of primary dendritic arm spacing during laser rapid directional solidification of single crystal nickel base superalloys

Prediction of Primary Dendritic Arm Spacing During Laser Rapid Directional Solidification of Single-Crystal Nickel-Base Superalloys

A Thermo-Metallurgical-mechanical Model for Selective Laser Melting of Ti6Al4V

Understanding the solute segregation and redistribution behavior in rapidly solidified binary Ti- X alloys fabricated through non-equilibrium laser processing

Laser Powder Bed Fusion of Titanium Aluminides: An Investigation on Site-Specific Microstructure Evolution Mechanism

An Integrated Modeling of Process-Structure-property Relationship in Laser Additive Manufacturing of Duplex Titanium Alloy

In Situ Prediction of Microstructure and Mechanical Properties in Laser-Remelted Al-Si Alloys: Towards Enhanced Additive Manufacturing

Effects of Annealing Temperature and Cooling Rate on Microstructures of a Novel Titanium Alloy Ti–6Al–2V–1.5Mo–0.5Zr–0.3Si Manufactured by Laser Additive Manufacturing

Optimization of Processing Parameters and Establishment of a Relationship Between Microstructure and Mechanical Properties of SLM Titanium Alloy

Solidification Behavior and Grain Morphology of Laser Additive Manufacturing Titanium Alloys

High-Throughput Technology Combining Machine Learning and Laser Additive Manufacturing to Investigate the Composition-Microstructure-Mechanical Property Relationships in Titanium Alloys

Cross-Scale Simulation Research on the Macro/Microstructure of TC4 Alloy Wire Laser Additive Manufacturing

Microstructure Evolution and Performance of Laser-Remelted Ti-6Al-4V Alloy

Investigation on solid-state phase transformation in a Ti-47Al-2Cr-2V alloy due to thermal cycling during laser additive manufacturing process

Numerical simulation of microstructural evolutions and prediction of mechanical properties in laser additive manufacturing

Prediction of Primary Dendrite Arm Spacing in Pulsed Laser Surface Melted Single Crystal Superalloy

Effects of Laser Processing Parameters on Microstructure and Mechanical Properties of Additively Manufactured AlSi10Mg Alloys Reinforced by TiC

Microstructure Evolution and Mechanical Properties of Laser Additive Manufactured Ti–5Al–2Sn–2Zr–4Mo–4Cr Alloy