Abstract:The nature of the interface between ceramic particle (CP) and metal matrix is critical to obtain solidification microstructures with optimal mechanical properties of CP-reinforced Al alloys in additive manufacturing. Generally, when the lattice misfit between the CP (e.g., TiB 2 ) and the α-Al matrix is higher than 4%, the interfacial coherency reduces, lowering the effectiveness of CPs. Here, we demonstrate that an L1 2 three-dimensional compound (3DC), which possesses lattice misfit with α-Al lower than 1%, can be introduced in between TiB 2 and α-Al via properly regulating the solidification cooling rate. In the 5TiB 2 /Al-4.5Mg-0.7Sc-0.2Zr (wt.%) as a model system, the lattice coherence of the TiB 2 /α-Al interface is tailored by introducing a 10-30 nm thick Al 3 (Sc,Zr) 3DC interphase when the cooling rate is increased to ~1000 o C/s. But, further increasing the cooling rate to ~6800 o C/s, only Al 3 (Sc,Zr) two-dimensional compound (2DC) with an apparent lattice strain forms at the interface. Taking advantage of the cooling rate (10 2 -10 3 o C/s) provided by laser direct energy deposition (L-DED), the low-misfit "TiB 2 /Al 3 (Sc,Zr) 3DC/α-Al" multi-structural interfaces are acquired, enabling the 3.56TiB 2 /Al-4.36Mg-0.72Sc-0.22Zr alloy as fabricated with L-DED to achieved improved strength-ductility synergy (yield strength 257 MPa, elongation 13.8%) due to the isotropically fine Al grain structure and the homogenous TiB 2 particle dispersion. The outcome of this study provides fundamental knowledge on designing "ceramic/coherent primary interphase/metal matrix" multi-structural interfaces to improve the mechanical properties of engineering metallic materials manufactured by rapid solidification techniques, such as DED additive manufacturing (AM).

Optimization of Processing Parameters and Microstructure Evolution of (TiB+La 2 O 3 )/Ti6Al4V Manufactured by Laser Melting Deposition

Microstructure and Wear-resistant Properties of in situ TiB-TiC Reinforced Titanium Matrix Composites by Laser Deposition Manufacturing

Formability, densification behavior and hierarchical grain structure of laser-directed energy deposition of TiB reinforced titanium matrix composites

Microstructure and Mechanical Properties of Ti60-Ti2alnb Functionally Graded Materials Fabricated by Laser Directed Energy Deposition

Microstructure and Mechanical Properties of Ti-6al-4v Components Fabricated by Laser Micro Cladding Deposition

Achieving near equiaxed α-Ti grains and significantly improved plasticity via heat treatment of TiB reinforced titanium matrix composite manufactured by selective laser melting

Enhancing Hardness and Wear Performance of Laser Additive Manufactured Ti6Al4V Alloy Through Achieving Ultrafine Microstructure

Achieving strength-ductility combination and anisotropy elimination in additively manufactured TiB/Ti6Al4V by in-situ synthesized network architecture with fine grains

Grain refinement and columnar-to-equiaxed transition of Ti6Al4V during additive manufacturing via different laser oscillations

Effect of TiB2 Addition on the Microstructure and Mechanical Properties of Laser-Directed Energy Deposition TiAl Alloy

Nanoscale engineering of low-misfit TiB 2 /Al 3 (Sc,Zr)/α-Al multi-interface to improve strength-ductility synergy for direct energy deposited aluminum alloy

Effect of TiB 2 on the microstructure and mechanical properties of TiAl alloy produced by laser direct energy deposition

Complete fine-equiaxed β-columnar grains in laser direct energy deposition of Ti–6Al–4V parts

Achieving Equiaxed Transition and Excellent Mechanical Properties in a Novel Near-β Titanium Alloy by Regulating the Volume Energy Density of Selective Laser Melting

Grain refinement of additive manufactured Ti-6.5Al-3.5Mo-1.5Zr-0.3Si titanium alloy by the addition of La2O3

Grain refinement and improved tensile properties of Ti5Al2Sn2Zr4Mo4Cr titanium alloy fabricated by laser solid forming

Microstructure evolution and underlying thermal behavior of high-content TiC reinforced titanium matrix composites fabricated by laser directed energy deposition

Columnar to Equiaxed Transition During Β Heat Treatment in a Near Β Alloy by Laser Additive Manufacture

Additive manufacturing of high-strength commercially pure titanium through lanthanum oxide addition

Microstructure and Mechanical Properties of An Ultrahigh-strength Titanium alloy Ti-4.5Al-5Mo-5V-6Cr-1Nb Prepared Using Laser Directed Energy Deposition and Forging: A Comparative Study

From gradient to homogenous: thermal behavior-induced microstructure evolution and mechanical properties of selective laser-melted TiB2p/2024Al composite