Enhancing Hardness and Wear Performance of Laser Additive Manufactured Ti6Al4V Alloy Through Achieving Ultrafine Microstructure

Yanqin Li,Lijun Song,Pan Xie,Manping Cheng,Hui Xiao

DOI: https://doi.org/10.3390/ma13051210

IF: 3.4

2020-03-08

Materials

Abstract:Refining microstructure is an important issue for laser additive manufacturing (LAM) of titanium alloy. In the present work, the microstructures of LAM-fabricated Ti6Al4V alloy were refined using a low energy density with the combination of a small spot diameter, a low laser power, and a high scanning speed. The microstructure, hardness, wear performance, and molten pool thermal behavior of LAM-fabricated Ti6Al4V coatings were studied. The results show that the grain sizes of both prior β and α phases are strongly dependent on the cooling rate of the molten pool. The fine prior β grains and submicron-scale acicular α phases were obtained under a low energy density of 75 J mm−2 due to the high cooling rate of the molten pool. In addition, the as-fabricated Ti6Al4V sample with submicron-scale acicular α phase showed a very high hardness of 7.43 GPa, a high elastic modulus of 133.6 GPa, and a low coefficient of friction of 0.48. This work provides a good method for improving the microstructure and mechanical performance of LAM-fabricated Ti6Al4V alloy.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is the microstructure optimization of Ti6Al4V alloy prepared by laser additive manufacturing (LAM) technology and the improvement of its hardness and wear - resistance performance. Specifically, the researchers used the method of low energy density combined with small spot diameter, low laser power and high scanning speed to refine the microstructure of Ti6Al4V alloy prepared by LAM. Through this method, they successfully obtained ultrafine grains and sub - micron - scale acicular α - phase. These microstructure characteristics significantly increased the hardness and elastic modulus of the material and reduced the friction coefficient, thus improving the wear performance of the material.

The key points mentioned in the paper include:
- **Refinement of microstructure**: By adjusting the LAM process parameters, especially using a low energy density (75 J mm\(^{-2}\)), the researchers obtained fine prior - β grains and sub - micron - scale acicular α - phase.
- **Improvement of mechanical properties**: The refined microstructure made the prepared Ti6Al4V samples have very high hardness (7.43 GPa), high elastic modulus (133.6 GPa) and a lower friction coefficient (0.48).
- **Relationship between thermal behavior and microstructure**: The study also explored the relationship between processing parameters, molten pool thermal behavior, microstructure and mechanical properties, and pointed out that a high cooling rate helps to promote martensitic transformation, further affecting the microstructure and properties of the material.

Overall, this paper aims to improve the microstructure of Ti6Al4V alloy by optimizing LAM process parameters, thereby improving its hardness and wear - resistance performance, which is of great significance for applications in aerospace, energy, biomedical and other fields.