Abstract:To improve the mechanical properties of Ti48Al2Cr2Nb (TiAl) alloys, Ti48Al2Cr2Nb-xTa alloy specimens without metallurgical defects were obtained by a laser additive manufacturing (LAM) technique using Ti48Al2Cr2Nb/Ta mixed powders as raw materials. The effects of different Ta contents on the microstructures, phase compositions, and tensile properties of the TiAl alloys were systematically investigated, and the relationship between these properties was established. The results showed that the lamellar structure was composed of α2 (Ti3Al), γ (TiAl), and β/B2 (β ordered to B2) phases. With the increase of Ta content, the thickness of the lamellar structure increased, and the lamellar length gradually shortened. The morphology of the α2 phase changed from an ultra-fine continuous lamellar structure to a short lamellar and an equiaxed structure. On the other hand, the morphology of the γ phase changed from lamellar to an equiaxed crystal structure, while the morphology of β/B2 phase changed from ellipsoid shape to fine block to coarse block structure. When the amount of Ta added to the TiAl powders was 0 at.%, 2 at.%, and 5 at.%, respectively, the tensile strength gradually decreased with the increase of temperature, while the elongation increased. When the amount of Ta was 8 at.%, the tensile strength at room temperature dropped to the minimum (393 MPa), and the elongation reached its maximum value (21.2%). Thus, it can be concluded that the 5 at.%Ta alloy had the best comprehensive tensile properties. The maximum tensile strength of the TiAl-5 at.%Ta alloy at room temperature, 750 °C and 850 °C, was 677 MPa, 651 MPa, and 538 MPa, respectively, and the elongation was 2.0%, 2.0%, and 13%, respectively. Compared with the TiAl-0 at.%Ta alloy, the tensile strength of TiAl-5 at.%Ta at room temperature, 750 °C, and 850 °C increased by 1.66, 2.08, and 1.9 times respectively, and the elongation increased by 1.43, 1.43, and 9.29 times, respectively.

Solidification Microstructure and Mechanical Properties of Laser Additive Manufactured Near-α Ti-6Al-3Nb-2Zr-1Mo Titanium Alloy

Investigation on the Microstructure and Mechanical Behaviors of a Laser Formed Nb-Ti-Al Alloy

Microstructure, texture and tensile properties as a function of laser power of Ti48Al2Cr2Nb5Ta alloy prepared by laser additive manufacturing

Microstructure and Mechanical Properties of Ti-6al-4v Components Fabricated by Laser Micro Cladding Deposition

Microstructure and mechanical properties of laser additive manufactured novel titanium alloy after heat treatment

In-situ Investigation of the Anisotropic Mechanical Properties of Laser Direct Metal Deposition Ti6Al4V Alloy

Achieving Ti-5Al-4Sn-2Zr-1Mo-0.25Si-1Nb Alloys with High Strength and Moderate Ductility through Selective Laser Melting

Effects of Tantalum on the microstructure and properties of Ti-48Al-2Cr-2Nb alloy fabricated via laser additive manufacturing

Microstructure and Mechanical Properties of An Ultrahigh-strength Titanium alloy Ti-4.5Al-5Mo-5V-6Cr-1Nb Prepared Using Laser Directed Energy Deposition and Forging: A Comparative Study

Microstructure and Mechanical Properties of Ti60-Ti2alnb Functionally Graded Materials Fabricated by Laser Directed Energy Deposition

Effect of annealing treatment on microstructure and tensile properties of Ti-48Al-2Cr-5Nb alloy fabricated by laser additive manufacturing

Electron Beam Welding and Post Heat Treatment of a New Near-Beta High-Strength Ti-4Al-5Mo-5V-5Cr-1Nb Alloy

Enhancing Hardness and Wear Performance of Laser Additive Manufactured Ti6Al4V Alloy Through Achieving Ultrafine Microstructure

Microstructure and Mechanical Property Improvement of Laser Additive Manufacturing Ti–6Al–4V via the Niobium Addition

Microstructure and mechanical properties of a newly developed Ti-6Al-2Mo-2Sn-2Zr-2Cr-2V alloy fabricated by laser directed energy deposition

Investigation on the Microstructure and Mechanical Properties of the Ti-Ta Alloy with Unmelted Ta Particles by Laser Powder Bed Fusion

Effect of Heat Treatment on the Microstructure and Mechanical Properties of Additive Manufactured Ti-6.5Al-2Zr-1Mo-1V Alloy

Simultaneous improvement of strength and ductility of laser additively produced Ti6Al4V by adding tantalum

Study of microstructure and compressive strength of a novel Ti-0.75Al-9.5V alloys manufactured by laser deposition melting

Experimental study on microstructural evolution, mechanical property, and corrosion behaviour of laser additive manufactured (LAM) titanium alloy grade 5

Grain refinement of additive manufactured Ti-6.5Al-3.5Mo-1.5Zr-0.3Si titanium alloy by the addition of La2O3