Effect of TiB 2 on the microstructure and mechanical properties of TiAl alloy produced by laser direct energy deposition

Hangyu Yue,Jibang Yang,Yunluo Wang,Kesong Miao,Youxing Yao,Jixin Yang,Xinliang Xie,Qi Chao,Guohua Fan
DOI: https://doi.org/10.1016/j.matchar.2024.113992
IF: 4.537
2024-05-22
Materials Characterization
Abstract:A Ti-48Al-2Cr-2Nb alloy was prepared by laser directed energy deposition (DED). The microstructure of the DED-produced Ti-48Al-2Cr-2Nb alloy exhibited a coarse columnar structure along the building direction. Through a combination of experiment and numerical simulation, the temperature gradient and solidification rate of the single-track sample were calculated theoretically. The columnar to equiaxed transition (CET) behavior of molten pool solidification was quantitatively analyzed, and the microstructure transition diagram was established. The effect of TiB 2 on the microstructure and mechanical properties of the TiAl alloy was investigated. The columnar changed to equiaxed grains in the vertical cross section by adding nanometer-sized TiB 2 particles and the microstructure was significantly refined. The grain size was reduced from 48.5 μm to 4.9 μm. Some equiaxed γ grains were distributed around the banded TiB 2 . The compressive properties were improved from 628.4 MPa to 698.8 MPa by adding nanometer-sized TiB 2 particles. Finally, the solidification behavior and the microstructure refinement mechanism caused by the addition of TiB 2 particles were discussed.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing
What problem does this paper attempt to address?