Abstract:Ti-2Al-2.5Zr alloy with hcp structure is a kind of structural materials used under low temperature condition, e.g. pipeline system of liquid hydrogen and liquid oxygen in missile engine. It is usually serviced in condition of severe low temperature and dynamic loading. Deformation twinning is a common and important plastic deformation mode in the hexagonal close-packed alloy., but will be severely restricted as the grain is refined from tens of microns to a few microns. On the other hand, twinning has a low sensitivity to temperature, consequently becomes a favorable deformation mode at low temperature in comparison with dislocation slip. The objective of this work is to study the coupling effect of grain refinement and testing temperature on twinning behavior and the low-cycle fatigue behavior of Ti-2Al-2.5Zr.Symmetrical push-pull low-cycle fatigue (LCF) tests were performed on Ti-2Al-2.5Zr with grain size of about 5 pm at room temperature (RT) and low temperature (77 K). The results show that the alloy exhibits the higher ductility and the longer low-cycle fatigue life at 77 K than those at RT. The cyclic stress response curves show that the cyclic softening occurs at the low strain amplitudes of 0.5% and 1.0%. However, as strain amplitude increased to 1.5% and 2.0%, cyclic stress saturation appeared. When testing temperature declined to 77 K, the cyclic hardening was observed at all four strain amplitudes. The degree of cyclic hardening increases as the strain amplitude rises. The fractography analyses suggest that transgranular fracture with well-developed fatigue striations is the predominant failure mode. The amount of secondary cracks is much higher in the alloys deformed at RT than that at 77 K. TEM examination reveals that deformation twins become more active. The primary types of twinning are {10 (1) over bar1} and {11 (2) over bar1}. The typical deformation microstructures consist of individual dislocation lines together with the tangled dislocation at the low strain amplitudes of 0.5% and 1.0%. As the strain amplitude increased to 1.5% and 2.0%, {10 (1) over bar0} prismatic slip and {11 (2) over bar1} pyramidal slip were simultaneously activated, the subgrain and dislocation cells were formed. At 77 K and strain amplitude of 2.0%, the parallel dislocation bands distribute along prismatic plane. As the strain amplitude increased to 4.5%, mutua l perpendicular dislocation lines appeared. The improvement of fatigue life of Ti-2Al-2.5Zr at 77 K is attributed to the constraint of inhomogeneous slip and the activation of deformation twinning.

Low cycle fatigue properties and microscopic deformation structure of Zircaloy-4 in recrystallized and stress-relieved conditions

On the mechanism of zircaloy-4 fatigue-deformation under different heat-treatment conditions

Low Cycle Fatigue Behavior and Deformation Mechanisms of Zirconium and Zircaloy-4

Microscopic Characterization on Low Cycle Fatigue Behavior at Room Temperature of Zircaloy-4 Alloy with Recrystallized Microstructure

Effect of test temperature on low cycle fatigue behavior of zircaloy-4

Cyclic deformation behavior of zircaloy-4 at different temperatures

High cycle fatigue properties and microstructure of zirconium and zircaloy-4 under reversal bending

Biaxial low cycle fatigue lifetime evaluation of zircaloy-4

Low-cycle fatigue behavior and deformation substructure of Ti-2Al-2.5Zr alloy at 673 K

Fatigue dislocation configurations in hexagonal Zircaloy-4

Biaxial low cycle fatigue properties and dislocation substructures of zircaloy-4 under in-phase and out-of-phase loading

Low-Cycle Fatigue Behavior and Deformation Substructure of Ti-2al-2.5zr Alloy at 298 and 673K

Deformation mechanism and cyclic stress response of Zircaloy-4 alloy cladding tube during low cycle fatigue at room temperature

Cyclic deformation behavior and dislocation substructures of hexagonal Zircaloy-4 under Out-of-Phase loading

HIGH CYCLE FATIGUE BEHAVIOR OF COMMERCIAL PURITY ZIRCONIUM UNDER CYCLIC REVERSED BEND LOADING

Biaxial Low Cycle Fatigue Properties of Zircaloy-4 under Tension-Torsional Proportional Loading

Low-cycle Fatigue Behavior and Deformation Substructure of Ti-2Al-2.5Zr Alloy at 673K

Dislocation Structures in Zirconium and Zircaloy-4 Fatigued at Different Temperatures

BIAXIAL FATIGUE BEHAVIOR AND MICROSCOPIC DE FORMATION MECHANISM OF ZIRCALOY-4 Ⅱ. Cyclic Deformation Substructures and Texture Development

Low Cycle Fatigue Failure Analysis of a Ni‐Based Single Crystal Superalloys at 850 °C

LOW CYCLE FATIGUE BEHAVIORS AND MICROSTRUCTURES OF Ti–2Al–2.5Zr WITH FINE GRAIN AT RT AND 77 K