Abstract:The fatigue behavior of as-cast Mg–12%Zn–1.2%Y–0.4%Zr alloy has been investigated. The S–N curve showed that the fatigue strength at 107 cycles was 45MPa. Scanning electron microscopy observations on the surfaces of the failed and unfailed specimens (after up to 1×107 cycles) suggested that the slip bands could act as preferential sites for non-propagating fatigue crack initiation, and the I-phase could effectively retard fatigue crack propagation (FCP). The macro fracture morphology clearly indicated that the overall fracture surface was composed of three regions, i.e. a fatigue crack initiation region (Region 1), a steady crack propagation region (Region 2) and a tearing region (Region 3). High-magnification fractographs showed that only porosities can act as the crack initiation sites for all specimens. Moreover, for specimens with fatigue lifetimes lower than 2×105 cycles, the cracks mostly initiated at the subsurface or surface of the specimen. However, when the fatigue lifetime was equal to or higher than 2×105 cycles, the fatigue crack initiation sites transferred to the interior of the specimen. The maximum stress intensity factors corresponding to the transition sites between Regions 1, 2 and 3 were 2 and 4.2MPam1/2, respectively. When the maximum stress intensity factor Kmax was lower than 4.2MPam1/2, in the steady crack propagation region, due to the retarding effect of I-phase/α-Mg matrix interfaces, the fatigue cracks tended to pass the I-phase/α-Mg matrix eutectic pockets directly and propagated through the grain cells, resulting in the formation of many flat facets on the fracture surface. However, when the maximum stress intensity factor was higher than 4.2MPam1/2, in the sudden failure region, the rigid bonding of I-phase/α-Mg matrix interfaces was destroyed and the cracks preferentially propagated along the interfaces, which resulted in the fracture surface being almost completely composed of cracked I-phase/α-Mg matrix eutectic pockets. Based on microstructural observation and the fracture characteristics of the two regions, it is suggested that with an increase in crack tip driving force, the FCP mode changes from transgranular propagation to intergranular propagation.

HIGH CYCLE FATIGUE BEHAVIOR OF COMMERCIAL PURITY ZIRCONIUM UNDER CYCLIC REVERSED BEND LOADING

Low Cycle Fatigue Behavior and Deformation Mechanisms of Zirconium and Zircaloy-4

High cycle fatigue properties and microstructure of zirconium and zircaloy-4 under reversal bending

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Fatigue-induced HCP-to-FCC Phase Transformation Assisting Crack Nucleation of Pure Zirconium in High Cycle Fatigue Regime

Micro-scale mechanism for cyclic deformation behavior in Zirconium under low-cycle-fatigue loading

Low cycle fatigue properties and microscopic deformation structure of Zircaloy-4 in recrystallized and stress-relieved conditions

Low Cycle Fatigue Behavior and Crack Initiation Mechanism of Ni-based Single Crystal Curved Thin-Walled Blade Simulator Specimen with Film Cooling Holes

Low Cycle Fatigue Failure Analysis of a Ni‐Based Single Crystal Superalloys at 850 °C

Fatigue-Induced HCP-to-FCC Phase Transformation Resulting in Two FCC-Zr Variants in Pure Zirconium

On the mechanism of zircaloy-4 fatigue-deformation under different heat-treatment conditions

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Cyclic deformation behavior of zircaloy-4 at different temperatures

Effect of test temperature on low cycle fatigue behavior of zircaloy-4

Microscopic Characterization on Low Cycle Fatigue Behavior at Room Temperature of Zircaloy-4 Alloy with Recrystallized Microstructure

Fatigue dislocation configurations in hexagonal Zircaloy-4

High Cycle Fatigue Behavior of Ti–5Al–5Mo–5V–3Cr–1Zr Titanium Alloy with Bimodal Microstructure

Research On The Cyclic Fatigue Behavior Of Zirconia Ceramics At The Room Temperature

Cyclic deformation behavior and dislocation substructures of hexagonal Zircaloy-4 under Out-of-Phase loading

The Fatigue Behavior of I-phase Containing As-Cast Mg–Zn–Y–Zr Alloy

Low cycle fatigue properties of refractory high-entropy HfNbTiZr alloy