Dislocation Structures in Zirconium and Zircaloy-4 Fatigued at Different Temperatures

Lin Xiao,Haicheng Gu

DOI: https://doi.org/10.1007/s11661-997-0232-1

1997-01-01

Metallurgical and Materials Transactions A

Abstract:The development of characteristic dislocation structures in pure zirconium and zircaloy-4 fatigued under pull-push strain control as the testing temperature and the cyclic strain range varied was examined using a thin-foil transmission electron microscopy (TEM) technique. The slip planes and the twinning planes were determined by a standard stereographic trace analysis technique. The first-order prismatic slip {10\(\bar 1\)0} is the primary deformation mode in zirconium and zircaloy-4 fatigued from room temperature (RT) to 873 K. The pyramidal sli {\(\bar 1\)2\(\overline {11} \)} is activated at 673 K and at high cyclic strain ranges, whereas the basal slip {0001} only appears in those specimens fatigued at 873 K. The {10\(\bar 1\)2}, {11\(\bar 2\)1}, and {11\(\bar 2\)2} types of twins were detected in specimens fatigued at RT. Twinning becomes less frequent as the testing temperature increases. The schematic map of the cyclic deformation modes as a function of the plastic strain range and the test temperature is described. The dislocation configurations in fatigued pure zirconium specimens evolve from a planar arrangement to a cell structure as the test temperature and the strain range increase. For zircaloy-4, the fatigued dislocation structure is parallel dislocation lines at RT, cells at 673 K, and two sets of approximate mutually perpendicular dislocation bands at 873 K, respectively. Finally, the fatigued dislocation-structure evolution map with the cyclic strain range and the test temperature are qualitatively established for zirconium and zircaloy-4, respectively. The effect factors on the fatigue mechanism and the thermodynamic and dynamic criteria of the dislocation-pattern evolution are discussed.