Effect of Cu content on the microstructure and properties of sintered Fe-0.8C-xCu antifriction materials
Jiaxin Li,Han Feng,Jianhua Zhang,Pengqi Chen,Jigui Cheng
DOI: https://doi.org/10.1088/2053-1591/ad72cf
IF: 2.025
2024-08-25
Materials Research Express
Abstract:Ferrous antifriction materials (FAMs) are important powder metallurgical antifriction materials. It is desirable to match the mechanical, friction and wear properties of Fe-0.8C-xCu parts for use in heavy-load applications. To study the effect of Cu content on the microstructure and properties of sintered Fe-0.8C-xCu antifriction materials, ferrous Fe-0.8C-xCu (x=5-25 wt. %) materials were prepared by powder metallurgy method. The density, microstructure, mechanical performance, friction and wear properties of the samples were investigated. The results showed that with an increase in Cu content, the relative density, hardness, friction and wear properties of sintered Fe-0.8C-xCu samples changed significantly. The Fe-0.8C-15Cu samples showed good comprehensive properties, with relative density, hardness, crushing strength, average friction coefficient and wear rate of 77.8 %, 43 HRB, 380 MPa, 0. 21 and 1.36×10-8 mm3/N·mm, respectively. The main wear mechanisms of the Fe-0.8C-xCu specimens are abrasive wear, adhesion wear, chafing fatigue, pitting, and oxidation. Effects of copper content on the microstructure and properties of Fe-0.8C-xCu (x=5-25 wt.%) materials with relatively high Cu content were investigated to obtain ferrous antifriction materials used under heavy load conditions.
materials science, multidisciplinary