Effect of Ni Content on Microstructure, Mechanical Properties, and Abrasion Behavior of Fe-B-C Alloy

Yanliang Yi,Jiandong Xing,Hongwan Jiang,Shaolei Long,Qiwei Wang

DOI: https://doi.org/10.1080/10402004.2023.2167141

IF: 2.056

2023-02-11

Tribology Transactions

Abstract:The microstructure, mechanical properties, and abrasion resistance of an Fe-2wt%B-0.35wt%C alloy with various Ni contents were analyzed. As the Ni addition increases, the Ni content of the matrix and M 2 B (M indicates Fe, Cr, and Mn) increases linearly with the relationships of y = 0.992 x and y = 0.224 x , respectively. With the Ni content increasing from 0 wt% to 1.2 wt%, the critical cooling rate of the alloy changes from 0.5 °C/s to 0.1 °C/s, which decreases the volume fraction of as-cast pearlite from 72.86 vol% to 3.49 vol%. Moreover, the Ni atom replacement is helpful in the formation of edge dislocation in the M 2 B, facilitating an increase in the toughness characteristic δ A of M 2 B from 2.85 to 3.04. Interestingly, when the Ni content is less than 0.9 wt%, the heat treatment makes a huge contribution to the macrohardness, bending stress, and abrasion resistance of alloy, owing to the formation of martensite. However, once the Ni content exceeds 0.9 wt%, heat treatment plays a negative role in the macrohardness, bending stress, and abrasion resistance of the alloy, because of the precipitation of M 23 (B,C) 6 .

engineering, mechanical