Abstract:Aligned multiwalled carbon nanotube (CNT) arrays were prepared using chemical vapor deposition of C2H4 on Fe catalyst at 750 °C. CNT array height and alignment depends strongly on the duration of H2 pretreatment, with optimal height and alignment achieved using 10-15 min pretreatment. Small-angle X-ray scattering (SAXS) was used to quantify the alignment, distribution, and size of the CNTs in arrays produced from varying pretreatment times and the results correlated with microscopy measurements. SAXS analysis revealed that the higher section of the CNT arrays exhibited better alignment than the lower section. Combining these insights with transmission electron microscopy measurements of the CNT defects within each array enable a mechanism for the CNT growth to be proposed, where the loss of alignment arises from deformation of the CNTs during their growth. Gas permeation test across densified CNT arrays indicated that the alignment of the CNT array plays an important role in the gas transport, and that the gas diffusion across the well-aligned CNT arrays was enhanced by a factor of ~45, which is much more than that across the poorly aligned CNT arrays, with an enhancement factor of ~8.

Preparation of aligned carbon nanotube arrays by pyrolysis of iron (II) phthalocyanine and ethylene

Preparation of tTree-branch-like aligned carbon nanotube array

Preferential Growth of Carbon Nanotubes/Nanofibers Using Lithographically Patterned Catalysts

The Fabrication And Characterization Of N-Doped Aligned Carbon Nanotube Arrays In Large Area

Preparation of High Purity Carbon Nano -Tubes from Ethylene Decomposition over Nanosized Iron- Based Catalysts

Production of Aligned Carbon Nanotube Films and Nitrogen Doped Carbon Nanotube Films from the Pyrolysis of Styrene

Effects of Temperature and Catalyst Concentration on the Growth of Aligned Carbon Nanotubes

Growth of aligned carbon nanotube arrays on metallic substrate and its application to supercapacitors

Large‐Scale Synthesis, Annealing, Purification, and Magnetic Properties of Crystalline Helical Carbon Nanotubes with Symmetrical Structures

The Fabrication of Macroscopical Long Aligned Carbon Nanotube Arrays

Synthesis and Magnetic Properties of Aligned Carbon Nanotubes by Microwave-Assisted Pyrolysis of Acetylene

J2240204 Evaluation of the Properties and Alignment of Carbon Nanotube Sheet Grown by CVD Method

Direct Growth of Horizontally Aligned Carbon Nanotubes Between Electrodes and Its Application to Field-Effect Transistors

Growth Of High-Quality Single-Wall Carbon Nanotubes Without Amorphous Carbon Formation

In-situ Purification of Aligned Carbon Nanotube Arrays by H_2O_2

Aligned Cnx Nanotubes By Pyrolysis Of Ferrocene/C-60 Under Nh3 Atmosphere

Fabrication of Aligned Carbon Nanotube Films and Its Field Emission Properties

Layered Growth of Aligned Carbon Nanotubes Arrays on Silicon Wafers

Field Emission from Carbon Nanotube Arrays Fabricated by Pyrolysis of Iron Phthalocyanine

Pretreatment Control of Carbon Nanotube Array Growth for Gas Separation: Alignment and Growth Studied Using Microscopy and Small-Angle X-ray Scattering.

THE GROWTH OF ALIGNED CARBON NANOTUBES ON FeNiCo CATALYST FILMS