Giant Magnetoresistance of Fe_x-C_(1-x) Films on Si Substrates

Zhang Xiaozhong,Xue Qingzhong

2006-01-01

Abstract:Fe_x-C_1-x films on n-Si substrates were prepared using pulsed laser deposition method.A novel type of magnetoresistance(MR) was found in Fe_x-C_1-x/Si.When T<258 K,MR of Fe_0.011-C_0.989/Si is negative and when 258 K<T<340 K,MR is positive.At T=300 K and B=1 T a large positive MR of 20% was found in Fe_0.011-C_0.989/Si.And the MR has different field dependences within the different temperature ranges: MRs at 280 and 300 K are positive and increase rapidly as the magnetic field(B) increases below B=1 T,and then MR increases slowly as the B increases,whereas MR at 350 K has a B~1.5 of field dependence.Contrary to the above MRs,MR at 30 K is negative and decreases as B increases.A two-channel model was proposed to explain novel MR.