Abstract:Co-C nanocomposite thin films with a Co atomic content of 13.0% were fabricated onto Si (100) substrates by magnetron co-sputtering technique. Post annealing was carried out in vacuum at annealing temperature ranging from 473 K to 773 K for 30 min. TEM images indicate that the Co nanoparticles are dispersed uniformly in an amorphous carbon matrix for the as-deposited samples, and Co particle size is in a range of 1.5-3.0 nm. After annealing at 673 K, the average Co particle size is enlarged distinctly. Magnetization hysteresis loops reveal that the as-deposited thin films show low magnetization. As annealing temperature is increased, both magnetization and coercivity are enhanced significantly. The samples annealed at 673 K and 773 K show ferromagnetic behaviors at low temperature, and superparamagnetic behaviors at room temperature, which are characteristic magnetic features for granular system. A negative magnetoresistance (MR) of 1.33% is observed for the as-deposited Co-C thin films at 4.2 K in the applied magnetic field of 3980 kA/m. The MR value decreases with increasing annealing temperature. Resistance (R) versus temperature (T) curves exhibit a good linear relationship of lnR-T-1/4 at a broad low temperature range, suggesting that the conduction in Co-C nanocomposite thin films follows the variable range hopping transport mechanism. © Copyright.

Giant Magnetoresistance of Co-Sio2 Nano-Granular Films

The Tunneling Magnetoresistance of Co-35(Sio2)(65) Nanogranular Films

The giant magnetoresistance and domain observation of Co35(SiO2)65 nano-granular film

Large magnetoresistance in Co-x-C1-x granular films on Si(100) substrate prepared by pulsed laser deposition

Magnetic Properties and Magnetoresistance of Co X C 1− X Granular Films Prepared by Magnetron Sputtering

Hall Effect Of (Co0.34fe0.66)(0.42)(Sio2)(0.58) Granular Films

Effect of SiO2 on the electromagnetic characteristics of lossy CoFeB-SiO2 nanogranular films

Preparation and Microstructures of CoAg Granular Films with Giant Magnetoresistance

Microwave Electromagnetic Characteristics of Fecob-Sio2 Nano-Granular Magnetic Films

Dependence of Giant Magnetoresistance on Microstructures in Ion-Beam Co-Sputtered Coxag1-X Granular Films

Study on GMR in CoAg Thin Granular Films

Percolation and Microwave Characteristics of CoFeB–SiO2 Nano-Granular Films

Microstructure, magnetic and magnetotransport properties of Co-C nanocomposite thin films

Giant Positive Magnetoresistance in Co@CoO Nanoparticle Arrays

Discussion on The Strong Uniaxial Anisotropy of Co40Fe40B20-SiO2 Nana-granular Films

Soft Magnetic Properties Of Sequential Deposited Co40fe40b20/Sio2 Multilayer Nanogranular Films For High Frequency Applications

Influence of Annealing Temperature on the Giant Magnetoresistance of Co-35(Sio2)(65) Nano-Granular Films

Magnetic Properties of FeSi-SiO2 Granular Films

Gmr and Characterization of Microstructures in Ion-Beam Cosputtered Coag Granular Films

TEMPERATURE AND SIZE DEPENDENT INTERPARTICLE INTERACTIONS IN Co-SiO2 GRANULAR FILMS

Giant Magnetoresistance and Microstructures in CoAg Granular Films Fabricated Using Ion-Beam Co-Sputtering Technique