Giant Magnetoresistance Properties in Granular Type (Co-Ag)/ag Multilayers
SM Zhou,Y Wang,WR Zhu,RJ Zhang,YX Zheng,QY Jin,LY Chen,B You,W Ji,A Hu,HR Zhai,HL Shen
DOI: https://doi.org/10.1063/1.366775
IF: 2.877
1998-01-01
Journal of Applied Physics
Abstract:The giant magnetoresistance of sputtered granular type (Co–Ag)/Ag multilayers with different Co content and sublayer thickness’ was studied. With an increasing Ag layer thickness, the magnetoresistance ratio ΔR/R first increases to reach a maximum and then decreases. With an increasing Co content in the magnetic layers, the maximum shifts towards a large Ag layer thickness. These phenomena can be attributed to the antiferromagnetic coupling between the Co clusters in neighboring Co–Ag layers. With an increasing Co–Ag layer thickness, ΔR/R increases monotonically for a small Co content in the magnetic layers, while for a large Co content, a maximum appears at a small magnetic layer thickness. It is suggested that the interplay of spin dependent scattering and the shunting effect in the Co–Ag layers results in the above thickness dependence.