Structural And Magnetic Studies Of Co1-Xnixcr2o4 (0 <= X <= 1)
D. Wang,M. F. Shu,L. H. Yin,X. W. Tang,P. Tong,X. B. Zhu,J. Yang,W. H. Song,Y. P. Sun
DOI: https://doi.org/10.1063/1.5087986
IF: 2.877
2019-01-01
Journal of Applied Physics
Abstract:We have investigated the structural, magnetic, and thermal transport properties of Co1-xNixCr2O4 (0 < x < 1) to check the evolution of structural and magnetic properties upon the introduction of the Jahn-Teller active ion Ni2+. The x <= 0: 95 samples can be indexed with a cubic lattice with the space group Fd3m, whereas the x = 0: 98 sample undergoes a cubic-tetragonal structural transition, and the x. 0: 98 samples belong to a tetragonal lattice with the space group I41-amd at room temperature. All these samples undergo a paramagnetic-ferrimagnetic transition at T-C. A spiral ferrimagnetic ordering at T-S is suppressed when the amount of Ni is increased, and the abnormal magnetization at T-S for the x = 0: 6 and 0.8 samples is not pronounced. The measurements of magnetic hysteresis reveal that the x = 0: 4 and 0.6 samples possess a rather large coercivity H-C compared with the x = 0 and 1 samples. Specifically, the x = 0: 4 and 0.6 samples undergo a short-range antiferromagnetic transition above T-C. The magnetic properties of the Ni-doped samples can be understood in terms of the magnetic structure model consisting of longitudinal and transverse magnetic sublattices. Published under license by AIP Publishing.