Abstract:Co-C nanocomposite thin films with a Co atomic content of 13.0% were fabricated onto Si (100) substrates by magnetron co-sputtering technique. Post annealing was carried out in vacuum at annealing temperature ranging from 473 K to 773 K for 30 min. TEM images indicate that the Co nanoparticles are dispersed uniformly in an amorphous carbon matrix for the as-deposited samples, and Co particle size is in a range of 1.5-3.0 nm. After annealing at 673 K, the average Co particle size is enlarged distinctly. Magnetization hysteresis loops reveal that the as-deposited thin films show low magnetization. As annealing temperature is increased, both magnetization and coercivity are enhanced significantly. The samples annealed at 673 K and 773 K show ferromagnetic behaviors at low temperature, and superparamagnetic behaviors at room temperature, which are characteristic magnetic features for granular system. A negative magnetoresistance (MR) of 1.33% is observed for the as-deposited Co-C thin films at 4.2 K in the applied magnetic field of 3980 kA/m. The MR value decreases with increasing annealing temperature. Resistance (R) versus temperature (T) curves exhibit a good linear relationship of lnR-T-1/4 at a broad low temperature range, suggesting that the conduction in Co-C nanocomposite thin films follows the variable range hopping transport mechanism. © Copyright.

Magnetic properties, microstructures and magnetoresistance effect in Co/Alq3 granular films

Magneto-optical kerr effect in Co/Alq 3 granular films

Magnetic Properties and Magnetoresistance of Co X C 1− X Granular Films Prepared by Magnetron Sputtering

Electrical Transport Properties of (coxal1−x)2o3−v Oxide Magnetic Semiconductor and Corresponding Co–Al2O3 Granular Films

Tunneling Magnetoresistance of Co Granules in AlN/Co/AlN Type Discontinuous Films

Structure, Magnetic Property and GMR Effects of Co-C Granular Thin Films

Microstructure and High Frequency Properties of Nanogranular CoAlO Thin Films

Preparation and Microstructures of CoAg Granular Films with Giant Magnetoresistance

Microstructure, Magnetic Properties and Giant Magnetoresistance of Granular Cu-Co Alloy

Dependence of Giant Magnetoresistance on Microstructures in Ion-Beam Co-Sputtered Coxag1-X Granular Films

MICROSTRUCTURE OF FeCo–Cu NANOGRANULAR FILMS WITH GIANT MAGNETORESISTANCE

Nanoparticle morphology in FeCo–Al2O3 granular films with tunneling giant magnetoresistance

The Hall Effect of Co0.35fe0.65-Al2o3 Nanogranular Films

The Effect of Substrate Temperature on the Microstructure and Tunnelling Magnetoresistance of FeCo–Al 2 O 3 Nanogranular Films

Structural, electron transportation and magnetic behavior transition of metastable FeAlO granular films

Tunneling Magnetoresistance Effect in Co/TPD Granular Films

Giant Magnetoresistance and Microstructure of Co-Cu and Feco-Cu Granular Films

Giant Magnetoresistance of CuCo Granular Films Electrodeposited in Magnetic Field

Giant Magnetoresistance And Microstructure Of Feco-Al2o3 Nanogranular Films

Giant Magnetoresistance of Co-Sio2 Nano-Granular Films

Microstructure, magnetic and magnetotransport properties of Co-C nanocomposite thin films