Microstructure, magnetic and magnetotransport properties of Co-C nanocomposite thin films

Ruihe Tang,Zhigang Yang,Chi Zhang,Bai Yang,Xiaofang Liu,y u ronghai

DOI: https://doi.org/10.3724/SP.J.1037.2010.00546

2011-01-01

Abstract:Co-C nanocomposite thin films with a Co atomic content of 13.0% were fabricated onto Si (100) substrates by magnetron co-sputtering technique. Post annealing was carried out in vacuum at annealing temperature ranging from 473 K to 773 K for 30 min. TEM images indicate that the Co nanoparticles are dispersed uniformly in an amorphous carbon matrix for the as-deposited samples, and Co particle size is in a range of 1.5-3.0 nm. After annealing at 673 K, the average Co particle size is enlarged distinctly. Magnetization hysteresis loops reveal that the as-deposited thin films show low magnetization. As annealing temperature is increased, both magnetization and coercivity are enhanced significantly. The samples annealed at 673 K and 773 K show ferromagnetic behaviors at low temperature, and superparamagnetic behaviors at room temperature, which are characteristic magnetic features for granular system. A negative magnetoresistance (MR) of 1.33% is observed for the as-deposited Co-C thin films at 4.2 K in the applied magnetic field of 3980 kA/m. The MR value decreases with increasing annealing temperature. Resistance (R) versus temperature (T) curves exhibit a good linear relationship of lnR-T-1/4 at a broad low temperature range, suggesting that the conduction in Co-C nanocomposite thin films follows the variable range hopping transport mechanism. © Copyright.