Giant Magnetoresistance of CuCo Granular Films Electrodeposited in Magnetic Field

赵林,樊占国,杨中东,高鹏,秦高梧

DOI: https://doi.org/10.3321/j.issn:1004-0609.2009.05.022

2009-01-01

The Chinese Journal of Nonferrous Metals

Abstract:CuCo granular films were prepared by electrodeposition in the stable magnetic field. The giant magnetoresistance and magnetic property of the films were studied. The composition and structure of the plating films were studied by XRD. The giant magnetoresistance of the films was measured by the four line method. Vibration sample magnetometer was used to measure the magnetic properties. The giant magnetoresistance results show that the magnetoresistance of CuCo granular films prepared at 0.6 T after annealing at 500 ℃ for 1 h increases by 25% than that prepared without magnetic field after vacuum annealing. The reasons are that the crystal grains of films prepared at 0.6 T are more compact, and the defects in the film such as impurity and inclusion are reduced by the magnetic field. The hysteresis loops indicate that the granular film presents the optimal magnetism after annealing at 500 ℃ for 1 h. The single magnetic domain of particle in the film is contributed to promote the giant magnetoresistance. When the CuCo granular films are electrodeposited in the stable magnetic field, the microstructure of CuCo granular films is improved and the better giant magnetoresistance effect is obtained.