Abstract:To understand the effect of Co addition on the modulated structure coarsening and discontinuous precipitation (DP) growth kinetics of Cu–15Ni–8Sn alloy, the experiments are carried out using optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscopy (TEM). Our results showed that the addition of Co in Cu–15Ni–8Sn alloy did not recover with a new second-phase associated with Co. During the aging treatment process, the addition of Co reduced the coarsening kinetics of the modulated structure, which was related to the equilibrium solid solubility (Xe) of Ni and Sn in Cu, diffusion coefficient of Ni and Sn in Cu (D), and to the interfacial energy (σ) of α-Cu matrix/L12. The decrease in values of Xe, D and σ were resulted in a slowdown of the coarsening kinetics. Further, the suitable addition of Co significantly inhibited the nucleation and growth of discontinuous precipitation (DP). The growth kinetics of DP for Cu–15Ni–8Sn-xCo alloy were evaluated using the Johnson-Mehl-Avrami-Kolmogorov equation. With the combination of the Arrhenius equation, the activation energies (Q) of the samples were 105.45 kJ/mol, 150.76 kJ/mol, 178.44 kJ/mol, 251.53 kJ/mol, and 148.89 kJ. Compared with cobalt-free alloy, cobalt-containing alloys exhibited greater activation energy, which suggested that the addition of Co can greatly inhibit the formation of DP. Furthermore, the addition of Co led to decrease in the thickness of the grain boundary and increase in the interlamellar spacing of the DP, which were considered to be the main reasons for suppressing the growth of DP.

Precipitation of nanoscale Co particles in a granular Cu–Co alloy with giant magnetoresistance

Microstructure, Magnetic Properties and Giant Magnetoresistance of Granular Cu-Co Alloy

Nano-scale precipitates formed in Cu-Co based alloys and their magnetic properties

Giant Magnetoresistance and Microstructure of Co-Cu and Feco-Cu Granular Films

Co-precipitated Ni/Mn Shell Coated Nano Cu-rich Core Structure: A Phase-Field Study

Structure and giant magnetoresistance of granular Co-Cu nanolayers prepared by cross-beam PLD

Giant Magnetoresistance and Microstructures in CoAg Granular Films Fabricated Using Ion-Beam Co-Sputtering Technique

Nanostructure and Giant Magnetoresistive Properties of Granular Systems

Giant Positive Magnetoresistance in Co@CoO Nanoparticle Arrays

Homogenizing Effects of Co on Multi-Scale Elemental Distribution in Ru-containing Ni-based Single Crystal Superalloys

Microstructural Characterization of CoAg Granular Films

Giant Magnetoresistance of CuCo Granular Films Electrodeposited in Magnetic Field

Crystallization Kinetics of Co-Finemet Amorphous Alloys and Magnetic Properties of Nanocrystalline Powder Cores

Microstructure, magnetic and magnetotransport properties of Co-C nanocomposite thin films

Giant Exchange Bias and Ferromagnetism in the CoO Shell of Co/CoO-MgO Core-Shell Nanoparticles

Crystallization kinetics and magnetic properties of Fe 63.5Co10Si13.5B9Cu 1Nb3 nanocrystalline powder cores

Preparation and Microstructures of CoAg Granular Films with Giant Magnetoresistance

Influence of Annealing Condition on Giant Magnetoresistance of FeCo–Cu Granular Films

Gmr and Characterization of Microstructures in Ion-Beam Cosputtered Coag Granular Films

The giant magnetoresistance and domain observation of Co35(SiO2)65 nano-granular film

The effect of Co addition on the modulated structure coarsening and discontinuous precipitation growth kinetics of Cu–15Ni–8Sn alloy