Study Of The Kerr Effect Of Coxag100-X Granular Films
Sy Wang,Wm Zheng,Dl Qian,Rj Zhang,Yx Zheng,Sm Zhou,Ym Yang,By Li,Ly Chen
DOI: https://doi.org/10.1063/1.369097
IF: 2.877
1999-01-01
Journal of Applied Physics
Abstract:A series of CoxAg100-x granular films was annealed at 100, 250, 400, and 500 degrees C, respectively. Both the dielectric function and polar Kerr effect were measured using a spectroscopic ellipsometer and a magneto-optical Kerr spectrometer in the 1.5-4.5 eV photon energy range. It was found that the Kerr effect was greatly enhanced with increasing annealing temperature, especially for those samples having low Co compositions. After annealing, the strong resonance peaks appear in the 3.7-4.1 eV range. For the typical sample with x = 6, the maximum Kerr rotation angle is about 0.26 degrees near 4.0 eV after annealing at 500 degrees C. Through data analysis, the large negative peak at about 3.85 eV is attributed to the plasma edge of Ag, and the positive peak near 4.0 eV is attributed to the new magneto-optical structure and the properties of the granular film. The larger short-wavelength Kerr effect will be useful for increasing magneto-optical data-storage density. (C) 1999 American Institute of Physics. [S0021-8979(99)29408-X].