Abstract:Reducing fabrication costs and increasing system performance are the primary objectives of contemporary SOFC developments and research. One of the efficient ways to address the design and durability difficulties is to lower the operating temperatures to the intermediate range (IT, 500–800 °C). La 0.595 V 0.005 Sr 0.4 CoO 3−∂ (LV05SC) perovskite cathode is investigated as a novel cathode for intermediate temperature solid oxide fuel cells (IT-SOFC). Anode-supported YSZ ((Y 2 O 3 ) 0.08 (ZrO 2 ) 0.92 ) and GDC (Gd 0.1 Ce 0.9 O 1.95 ) electrolytes were prepared by a multilayer tape casting and co-firing method. The green bi-layer tapes were co-fired at various temperatures with optimized electrolyte and anode slurries. X-ray Diffraction (XRD) and Scanning Electron Microscopy (SEM) were used to analyze the microstructures and the phase characterizations of the cathode material and single cell. At 1250 °C of the co-firing temperature, as-prepared anode-supported cells showed no defects and excellent microstructural properties such as no gas permeability, porosity, and sintered structure. The electrolytes with a thickness of almost 20 μm were fairly dense. The power densities were evaluated and both anode-supported electrolytes showed good electrochemical performance at intermediate temperatures. The peak power density of the cell reached 89 mW/cm 2 , and the total resistance was only 3.05 Ω.cm 2 under open circuit conditions at 800 °C. The diffusion processes of oxide ions (O 2− ) were found to be the limiting step for ORR by the EIS analysis. These findings suggest that the compound is a promising cathode material for IT-SOFCs.

Intermediate-temperature SOFCs with Thin Ce0.8Y0.2O1.9 Films Prepared by Screen-Printing

YSZ Thin Films Prepared by a Novel Powder Coating Process on Porous NiO-YSZ Cermet

A high performance intermediate temperature fuel cell based on a thick oxide–carbonate electrolyte

A simple and easy one-step fabrication of thin BaZr0.1Ce0.7Y0.2O3−δ electrolyte membrane for solid oxide fuel cells

Conductivity Of Yttria-Doped Ceria Electrolyte Made By Chemical Coprecipitation And Its Evaluation For Sofc Application

Development of yttria-stabilized zirconia thin films via slurry spin coating for intermediate-to-low temperature solid oxide fuel cells

A cathode-supported SOFC with thin Ce0.8Sm0.2O1.9 electrolyte prepared by a suspension spray

Preparation of Thin Electrolyte Film Via Dry Pressing/heating/ Quenching/calcining for Electrolyte-Supported SOFCs

Fabrication and performance analysis of A-site metal-promoted La0.595V0.005Sr0.4CoO3−∂ perovskite oxides as cathodes for intermediate temperature solid oxide fuel cells

Sputter-deposited medium-temperature solid oxide fuel cells with multi-layer electrolytes

Fabrication and Properties of Anode-Supported Solid Oxide Fuel Cell

Boosting intermediate temperature performance of solid oxide fuel cells via a tri‐layer ceria–zirconia–ceria electrolyte

Fabrication and Electrochemical Characterization of Anode-Supported Microtubular Solid Oxide Fuel Cells Based on Ce0.8sm0.2o2-D Electrolytes

High Performance Solid Oxide Fuel Cells Based on Tri-Layer Yttria-Stabilized Zirconia by Low Temperature Sintering Process

Performances of YBaCo1.4Cu0.6O5+δ–Ce0.8Sm0.2O1.9 Composite Cathodes for Intermediate-Temperature Solid Oxide Fuel Cells

Fabrication and Performance of Anode-Supported Electrolyte Thin Films SOFCs

Fabrication and Characterization of Composite Electrolyte for Intermediate-Temperature SOFC

Low Temperature Deposited (ce,gd)o2−x Interlayer for La0.6Sr0.4Co0.2Fe0.8O3 Cathode Based Solid Oxide Fuel Cell

Development of Novel Low-Temperature SOFCs with Co-Ionic Conducting SDC-carbonate Composite Electrolytes

Preparation of SDC Interlayer and Influence on Performances of Anode Supported Solid Oxide Fuel Cells

Hierarchically oriented macroporous anode-supported solid oxide fuel cell with thin ceria electrolyte film.