Abstract:In this work, the WC-Cr2(C, N)-Co nanocomposites were synthesized by using the one-pot carbothermal reduction nitridation hydrothermal precursor method. The preparation mechanisms, including phase and morphology evolutions, were investigated by differential thermal analysis (TG-DSC), X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and thermodynamic analysis. The results showed that phase evolution, with temperature increasing, follows the sequences of (amorphous phase, WO2.72) → (CoWO4, WO2.72, WO2, CrWO3) → (WO2, CoWO4, Co6W6C, CrWO3) → (W2C, Co3W3C, WC) → (WC, W2C, Co3W3C) → (WC, Co, Co3W3C trace amount). Through comparing different heat treatment conditions, the powder particle size was more easily affected by temperature than holding time. The higher temperatures or longer time holding resulted in the aggregation of powder particles. Finally, WC-Cr2(C, N)-Co nanopowders with about 60 nm were obtained at 1050 °C for 1 h under the N2 flow of 1 L/min with the oxygen content of 0.22 wt% and the free carbon content of 0.19 wt%. The TEM elements mapping revealed that Cr distributes uniformly with WC grains, Co and WC grains are combined well. The surface of WC-Cr2(C, N)-Co determined by XPS is mainly composed of W, Co, Cr, C, N, and O. The spark plasma sintering (SPS) sintered WC-Cr2(C, N)-Co composite shows a nanocrystalline microstructure with the average grain size ∼170 nm, and the excellent comprehensive mechanical properties with the Vickers hardness 1730 Kg·mm−2 and fracture toughness 11.5 MPa·m1/2, respectively.

Study of Preparing Nanocystalline WC Powder

Preparation of Nanoscale WC Powders by Sol-Gel Synthesis and Carbon Monoxide Carbonization

Preparation of nano-scaled WC powder by low-temperature carbothermic reduction method

Feasible Production of Highly Homogeneous Nano-Scaled WC Powders: an Industrial Practice Via Raw Material Pretreatment and Direct Reduction-Carbonization

Study on the preparation mechanism of novel WC-Cr2(C, N)-Co nanocomposites

Synthesis of WC-0.67wt.%Cr<sub>3</sub>C<sub>2</sub> nanopowders by a one-step reduction-carbonization method and their characterization

Synthesis of WC-0.67wt.%Cr3C2 nanopowders by a one-step reduction-carbonization method and their characterization

Synthesis of Tungsten Carbide Nanopowder by a One-Step Carbothermal Reduction-Carbonization Method

Preparation of Ultra-Fine WC-Co Cermet and Its Wear Behavior

Preparation Technology of Ultra-Fine Tungsten Carbide Powders: an Overview

Preparation of Ultrafine Nanosized Tungsten Carbide by Hydrothermal Synthesis of Tungsten Precursor,Carbother-mic Reduction,and Carburization

Preparation of η phase powder and the effect of sintering process on the plate-like WC grain

Preparation of Ultrafine WC-10Co Composite Powders by Reduction and Carbonization

Study on influencing factors and mechanism of high-quality tungsten carbide nanopowders synthesized via carbothermal reduction

Synthesis and Characterization of WC-6Co Nanocrystalline Composite Powder

Synthesis and characterization of WC-Co nanosized composite powders with in situ carbon and gas carbon sources

Preparation of Nanocrystalline Tungsten Powder and Study of Its Sinterability

Analysis on Calcination Process of WC–Co Precursor Powder

The Synthesis of High Quality Coarse WC Powder by Two-step Carbonization

A New Route For The Preparation Of Tungsten Carbide-Cobalt Nanocomposites

Research on Preparation of Nanocrystalline TiC Powers