Abstract:Bismuth ferrite nano‐ and microcrystals were prepared by a facile molten salt technique in two kinds of molten‐salt‐based systems (NaCl–KCl and NaCl–Na2SO4). In the NaCl–KCl salt system, a systematic study indicating the effects of process parameters (e.g., calcination temperature, holding time as well as the molten salt ratios) on the bismuth ferrite formation mechanism and structural characteristics is reported. The results show that almost pure phase BiFeO3 powders with minimum impurity phase of Bi2Fe4O9 were synthesized at temperatures of 700°C–800°C, whereas high calcination temperature (e.g., 900°C) resulted in the formation of almost pure phase Bi2Fe4O9 powders. The prolonged holding time increased the particle size via the Ostwald ripening mechanism; however, there was little effect on the particle morphology. Similar phenomenon occurred as increasing the molten salt ratios. In the NaCl–Na2SO4 salt systems, it is found that low NP‐9 (nonylphenyl ether, NP‐9) surfactant content (0–5 mL) led to the formation of almost pure phase BiFeO3 powders, whereas high NP‐9 surfactant content (e.g., 20 mL) resulted in pure phase Bi2Fe4O9 powders. The average particle size of the BiFeO3 powders was decreased as increasing the NP‐9 surfactant content, whereas their morphologies did not change significantly. Because of the simplicity and versatility of the approach used, it is expected that this methodology can be generalized to the large‐scale preparation of other important transitional metal oxides with controllable sizes and shapes.

Effects of ZnCl2 addition on the ZnNb2O6 powder synthesis through molten salt method

Molten Salt Synthesis of ZnNb{sub 2}o{sub 6} Powder

Molten salt synthesis of ZnNb2O6 powder

Synthesis of ZnNb2O6 powder with rod-like particle morphologies

Synthesis of ZnO Nano-crystal Powder by Molten Salt Method

ZnTiO_3 Powder Prepared by Molten Salt Methods

Low Temperature Synthesis of ZnNb2O6 Fine Powders by Wet-Chemical Processes

Synthesis of complex niobate nanostructures via molten-salt reaction: Effect of ZrO 2 on product morphology

Molten Salt Synthesis, Characterization, and Formation Mechanism of Superfine (hfxzr1‐x)b2 Solid‐solution Powders

Molten Salt Synthesis of Bismuth Ferrite Nano‐ and Microcrystals and Their Structural Characterization

Low-Temperature Rapid Synthesis of LiNbO3 Powder by Molten Salt Methods

Synthesis of Bi0.5(Na0.7K0.2Li0.1)0.5TiO3 powders through the molten salt method

Synthesis Of Nio Nano-Crystal Powders By Molten Salt Method

Synthesis of Ti0.2Zr0.8B2 Solid‐solution Nanopowders by Molten Salt Assisted Borothermal Reduction

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Molten salt synthesis of rod-like tungsten bronze niobate particles

Effect of Raw Material Particle Size on the Synthesis of La 2 Zr 2 O 7 by the Molten Salt Method

Molten Salt Synthesis, Formation Mechanism, and Oxidation Behavior of Nanocrystalline HfB 2 Powders

A New Sight on The Influence of Molten Salt in The Preparation of (Ta, Nb, Ti) C Nano‐Powder

Synthesis of zirconium boride (ZrB2) rod crystals through salt-assisted boro/carbothermal reduction

Salt-assisted Low Temperature Solid State Synthesis of High Surface Area CoFe2O4 Nanoparticles