Abstract:The traditional quenching-tempering process is unable to satisfy the requirement of combination mechanical property of high strength steel along with low cost.Speer et.al.suggested a quenching-partitioning(Q-P)process,i.e.,holding certain duration at certain temperature after quenching,causing carbon partitioning from martensite to retained austenite.Carbon partitioning makes carbon enrichment and austenite stabilization in order to ensure the plasticity and toughness of high strength steel.In 2007,the present author proposed a novel heat treatment process,quenching-partitioning-tempering(Q-P-T)process,based upon the Q-P process,i.e.after quenching to Ms-Mf,beside the carbon partitioning,there is also a tempering procedure,that is,holding at certain temperature for certain duration in order to enhance the complex carbide precipitation and the strengthening reaction.The Q-P-T steel contains 0.5wt%C to prevent embrittlement,1.5wt%Si to suppress the cementite precipitation and to promote the carbon partitioning,(1.0-1.5)wt% alloying element Mn(Ni)to lowering Ms temperature as well as small amount of complex carbide forming elements Nb and Mo.Q-P-T steel with 0.48wt%C has shown the ultimate tensile strength of 2 160 MPa and total elongation of 11% treated by Q-P-T.Q-P-T steel with 0.2wt%C developed ultimate tensile strength of 1 150 MPa and total elongation of 17% and 0.1wt%C Q-P-T steel shows 900 MPa and good toughness respectively.Thermodynamics and kinetics of Q-P-T process are preliminarily considered.Further work is required to optimize the composition and heat treatment parameter for the Q-P-T steel.

Quenching-Partitioning-Tempering(Precipitation)(Q-P-T) Process for Ultra-high Strength Steel

Ultra-high Strength Steel Treated by Using Quenching–Partitioning–Tempering Process

A Brief Introduction to Quenching-Partitioning-tempering(q-p-t) Process

Strengthening and toughening mechanisms of quenching–partitioning–tempering (Q–P–T) steels

The investigation of ultra-high strength steel by quenching-partitioning- tempering (Q-P-T) process

Study of a Novel Ultra-High Strength Steel with Adequate Ductility and Toughness by Quenching-Partitioning-Tempering Process

Novel Ultrahigh-Strength Nanolath Martensitic Steel by Quenching–partitioning–tempering Process

Quenching-partitioning-tempering and Multicycle Quenching-partioning-tempering Processes

Ultrahigh strength-ductility steel treated by a novel quenching–partitioning–tempering process

Enhancement of the mechanical properties of a Nb-microalloyed advanced high-strength steel treated by quenching–partitioning–tempering process

Application of Quenching-Partitioning-Tempering Process in Hot Rolled Plate Fabrication

Property and Microstructure of a Novel Q-P-T Steel

Room-Temperature Quenching and Partitioning Steel

Characterization of Microstructure and Mechanical Properties of a Nb-Microalloyed Steel after Quenching-Partitioning-Tempering Process

Relationship Between Microstructure and Mechanical Properties of M50 Ultra-High Strength Steel Via Quenching-Partitioning-tempering Process

Quenching-Partitioning-Tempering Process and Its Engineering Feasibility of 900 MPa Grade Hot-Rolled Plate

The Mechanism of High Strength-Ductility Steel Produced by A Novel Quenching-Partitioning-Tempering Process and the Mechanical Stability of Retained Austenite at Elevated Temperatures

High Strength Ductility Steels Treated by Novel Quenching–partitioning–tempering Process

A Carbide-Free Bainite/martensite/austenite Triplex Steel with Enhanced Mechanical Properties Treated by a Novel Quenching–partitioning–tempering Process

Mechanism exploration of an ultrahigh strength steel by quenching-partitioning-tempering process

The Microstructural design and control of ultrahigh strength-ductility martensitic steels based on a novel quenching-partitioning-tempering process