One-pot Synthesis of Monodisperse CeO2 Nanocrystals and Superlattices

Ziyang Huo,Chen,Xiangwen Liu,Deren Chu,Haohang Li,Qing Peng,Yadong Li

DOI: https://doi.org/10.1039/b803215g

IF: 4.9

2008-01-01

Chemical Communications

Abstract:Monodisperse CeO(2) nanocrystals and superlattice-like colloidal particles have been successfully synthesized in ethanol-water mixed solvent by adopting a one-pot approach using icosahedral (NH(4))(2)Ce(NO(3))(6) as precursor.

What problem does this paper attempt to address?

Solvothermal Synthesis, Electrochemical and Photocatalytic Properties of Monodispersed CeO2 Nanocubes

Liwu Qian,Jun Zhu,Weimin Du,Xuefeng Qian

DOI: https://doi.org/10.1016/j.matchemphys.2009.02.047

IF: 4.778

2009-01-01

Materials Chemistry and Physics

Abstract:Cubic-like CeO2 nanocrystals were successfully synthesized through an improved-toluene solvothermal process using hexadecylamine (HAD) as a capping agent and CeCl3·7H2O as a precursor at 180°C for 24h. These nanocubes are about 10nm in size, and have a tendency to assemble into 2D superstructure. The obtained samples were characterized by means of X-ray powder diffraction (XRD) and transmission electron microscopy (TEM). It was found that the water content, the concentration of ligand and kinds of aliphatic amine played important roles in the formation of the novel morphology. A possible formation mechanism was proposed based on the controlling reaction parameters. The electrochemical and photocatalytic properties of the as-synthesized samples exhibited the size/shape-dependent properties and potential applications.
Facile Synthesis of Ceria Nanocrystals with Tuneable Size and Shape

Li Can,Luan Yiliang,Zhao Bo,Kumbhar Amar,Zhang Fan,Fang Jiye

DOI: https://doi.org/10.1557/adv.2020.25

2020-01-01

MRS Advances

Abstract:Ceria (CeO2) possesses a distinctive redox property due to a reversible conversion to its nonstoichiometric oxide and has been considered as a promising catalyst in the oxidative coupling of methane. Since a heterogeneously catalytic process usually takes place only on the surface of catalysts, it is reasonably expected that the performance of a catalyst, such as CeO2, highly relies on its size- and shape-dependent surface structure. We report our recent progress in achieving exclusive crystal facet-terminated CeO2 nanocrystals using a shape-controlled synthesis protocol in a one-pot colloidal system. We modified a two-phase solvothermal approach to fabricate cubic and truncated octahedral CeO2 nanocrystals with a size-control. During the two-phase solvothermal process, we propose that the Ce-precursors transfer from the aqueous layer to the interface of the organic phase, promoted by the capping ligands (as known as phase-transfer catalysts), for the oxidation and nucleation, and subsequently form CeO2 nanocrystals in the organic layer. As different capping ligands favor binding on diverse crystal facets, tuning the composition of the capping ligand with a precise control could generate nanocrystals that are dominated by a single type of facets with a relatively narrow size distribution.
Sustainable and Facile Route to Nearly Monodisperse Spherical Aggregates of CeO2 Nanocrystals with Ionic Liquids and Their Catalytic Activities for CO Oxidation

Zhen-Xing Li,Le-Le Li,Quan Yuan,Wei Feng,Jun Xu,Ling-Dong Sun,Wei-Guo Song,Chun-Hua Yan

DOI: https://doi.org/10.1021/jp807348n

2008-01-01

The Journal of Physical Chemistry C

Abstract:This article reports a novel preparation of nearly monodisperse spherical aggregates of CeO2 nanocrystals by using ionic liquid (1-hexadecyl-3-methylimidazolium bromide, C(16)MimBr) as both template and solvent. The products were characterized with X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), high-resolution TEM (HRTEM), X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, UV-vis spectroscopy, FT-IR spectroscopy, and N-2 adsorption-desorption methods. The spherical aggregates, with average diameter of 100 - 150 nm, are composed of ca. 3.5 nm CeO2 nanocrystals as building units, giving rise to three-dimensional (313) open porous structures with high Brunauer-Emmett-Teller surface area of 119 m(2).g(-1). Mesoporous CeO2 with surface area up to 227 m(2).g(-1) was prepared by simply tuning the amount of the ionic liquids. Loaded with 5 wt% CuO, both the spherical aggregates and the mesoporous CeO2 exhibit high catalytic activities for CO conversion with 100% conversion rates at low temperature of 150 degrees C, suggesting potential applications in preferential oxidation (PROX) and water-gas shift reaction (WGSR). This sustainable and facile method may be extended to the preparation of other metal oxide nanoarchitectures and provides guidance for structure-controlled synthesis.
Preparation of CeO2 Nanocrystals by Solvothermal Routes

YU Li-li,LIU Bao,QIAN Li-wu,QIAN Xue-feng

2010-01-01

Abstract:CeO2 nanocrystals were successfully synthesized via a simple alcohol-water solvothermal method using PVP as a capping agent and Ce(NO3)3·6H2O as a precursor.The shape and size of the products could be effectively tuned by controlling the reaction conditions,such as reaction time and the molar ratio of Ce3+to PVP.X-ray diffraction analysis showed that the phase of the particles was CeO2 of cubic system,and their structures and size were characterized by SEM and TEM.The results of photoluminescence(PL) spectra showed that the fluorescence peak corresponds to different luminescence centers,and the fluorescence of Eu3+∶CeO2 nanomaterials have excellent photoluminescence.
Controllable synthesis of nearly monodisperse spherical aggregates of CeO2 nanocrystals and their catalytic activity for HCHO oxidation.

Qin Wang,Wenjing Jia,Baocang Liu,Wenzhi Zhao,Changyan Li,Jun Zhang,Gang Xu

DOI: https://doi.org/10.1002/asia.201200432

2012-01-01

Chemistry - An Asian Journal

Abstract:Herein, we report a facile surfactant-assisted solvothermal synthetic method to prepare nearly monodisperse spherical CeO2 nanocrystals. A good control of the size of CeO2 nanocrystals in the range of 100-500 nm was achieved by simply varying the synthetic parameters such as reaction time, volume ratio of ethanol to water (R), molar ratio of PVP, and concentration of Ce(NO3)(3)center dot 6?H2O in solution. A possible mechanism for the growth of spherical CeO2 nanocrystals is proposed. The obtained CeO2 nanocrystals with a surface area of up to 47 m2g-1 were then employed as a catalyst support. By loading Au-Pd nanoparticles (about 3 wt.?%) onto the CeO2 support, an Au-Pd/CeO2 catalyst was prepared that exhibited high catalytic activity for HCHO oxidation. At the low temperature of 50 degrees C, the percentage of HCHO conversion was 100%, suggesting potential applications in preferential oxidation and other catalytic reactions. These Au-Pd/CeO2 catalysts may also find applications in indoor formaldehyde decontamination and industrial catalysis. The facile solvothermal method can be extended to the preparation of other metal oxide nanocrystals and provides guidance for size- and morphology-controlled synthesis.
One Step Hydrothermal Synthesis of CeO2–ZrO2 Nanocomposites and Investigation of the Morphological Evolution

Xiaohui Zhang,Qiang Wang,Jing Zhang,Jigang Wang,Ming Guo,Shaowei Chen,Chunhong Li,Changwen Hu,Youchang Xie

DOI: https://doi.org/10.1039/c5ra19271d

IF: 4.036

2015-01-01

RSC Advances

Abstract:Uniform cauliflower-like and rough nano-spheres of CeO2–ZrO2 composites were synthesized by a facile hydrothermal process using only urea as a mineralizer without any surfactant or template.
A New Method to Preparing Monodisperse CeO_2 Nanoparticles

Huan Li

2000-01-01

Abstract:The monodisperse CeO 2 nanoparticles were prepared by using modified two phase liquid-liquid method, the morphology and structure were characterized by transmission electron microscopy and X-ray diffraction methods.
Wet chemical preparation of well-dispersed colloidal cerium oxide nanocrystals

H. Maeda,Shengtai He,M. Uehara,Yulan Liu

DOI: https://doi.org/10.1246/CL.2007.764

2007-05-19

Abstract:In this study, a simple one-step wet chemical method was presented to prepare colloidal cerium oxide, CeO 2 , nanocrystals. By a direct decomposition of cerium(IV) ammonium nitrate in a solution of 1-octadecene and oleylamine at 180°C, well-dispersed CeO 2 nanoparticle colloid, with an average size of about 4.5 nm, was obtained.

Chemistry,Materials Science
Controlled Synthesis of CeO2 Nanoparticles from the Coupling Route of Homogenous Precipitation with Microemulsion

YJ He,BL Yang,CX Cheng

DOI: https://doi.org/10.1016/s0167-577x(02)01093-5

IF: 3

2003-01-01

Materials Letters

Abstract:CeO2 nanoparticles with good monodispersity and narrow size distribution were synthesized by the combined method of homogenous precipitation with microemulsion. The affect factors of preparing conditions were investigated. The products were characterized by XRD, TEM, FTIR, DTA and TGA. It was found that the average size of CeO2 nanoparticles could be tailored by adjusting the precipitation temperature, calcination temperature, and the sort of surfactants or the relative concentration of reactants.
The Synthesis of Nanometer Sized CeO2 Particles by the Coupling Route of Microemulsion with Homogeneous Precipitation

贺拥军,杨伯伦

DOI: https://doi.org/10.3969/j.issn.0441-3776.2003.02.014

2003-01-01

Abstract:CeO2 nanoparticles with good monodispersity and narrow size distribution were synthesized hy the coupling route of W/O microemulsion with homogenous precipitation. The morphology, size, size distrbution and the crystal structure of CeO2 nanoparticles were inspected. It was found that the sort of surfactants and the relative initial concentration of reactants have regular affections on the average size of products. The average size of products increases sharply with the calcination temperature. Research results may present a promising method for the synthesis of nanoparticles with controlled size and size distribution.
General and facile synthesis of ceria-based solid solution nanocrystals and their catalytic properties

Huan-Ping Zhou,Rui Si,Wei-Guo Song,Chun-Hua Yan

DOI: https://doi.org/10.1016/j.jssc.2009.07.002

IF: 3.3

2009-01-01

Journal of Solid State Chemistry

Abstract:Uniform Ce1−xZrxO2 (x=0.2–0.8) nanocrystals with ultra-small size were synthesized through a thermolysis process, facilitated by the initial formation of precursor (hydrated (Ce,Zr)-hydroxides) at low temperature. TEM, XRD, EDAX, and Raman spectra were employed to study the formation of the solid solutions with various Ce/Zr ratios. Ultraviolet–visible (UV–vis) spectra showed that the ratios of Ce3+ to Ce4+ in both surface and bulk for the as-prepared Ce1−xZrxO2 nanocrystals increased with the zirconium content x. The well-distributed Zr and Ce in the hydrated (Ce,Zr)-hydroxides before their thermolysis became the crucial factor for the structural homogeneity of the products. In addition, this strategy was extended to the synthesis of Ce1−xGdxO1−x/2, Ce1−xSmxO1−x/2, and Ce1−xSnxO2 solid solutions. Catalytic measurements indicated that the ceria-based catalysts were active for CO oxidation at temperatures beyond 250°C and the sequence of catalytic activity was Ce0.5Zr0.5O2>Ce0.8Zr0.2O2>Ce0.2Zr0.8O2>Ce0.5Sm0.5O1.75.
Mesoporous-shelled CeO2 hollow nanospheres synthesized by a one-pot hydrothermal route and their catalytic performance

Xueying Zhang,Lu-Lu Han,Wei Liu,Yanzhao Yang,Cong Zhang,Hongxiao Yang,Shuping Wang,Xiufang Liu

DOI: https://doi.org/10.1039/C3CE40959G

2013-09-10

Abstract:Uniform-sized and monodisperse CeO2 mesoporous hollow nanospheres composed of ceria nanocrystals were synthesized via a template-free and surfactant-assisted benign hydrothermal route. On the basis of a time-dependent experiment, the precipitation–dissolution–renucleation–assembly and Ostwald ripening processes mechanism is proposed for the formation of the CeO2 mesoporous hollow spheres. Poly(vinyl-pyrrolidone) (PVP) was applied as a surfactant to facilitate the reassembly of the CeO2 nanoparticles and the formation of the mesoporous shell of the hollow nanospheres. By increasing the amount of PVP, the mesoporous shell of the hollow spheres could be fabricated and became more apparent. Meanwhile, altering the amounts of H2O2 could control the size of the primary nanocrystals via affecting the nucleation/growth process of them, which is another key factor in the formation of the hollow structure and the uniform, monodispersed nanoparticles. The catalytic test results show that the as-obtained CeO2 mesoporous hollow spheres exhibited desirable CO catalytic properties. The synthesized Au–CeO2 nanospheres demonstrate a higher catalytic activity in CO oxidation than pure ceria nanospheres.

Chemistry,Materials Science
Template-Free Synthesis Of Single-Crystalline-Like Ceo2 Hollow Nanocubes

Guozhu Chen,Caixia Xu,Xinyu Song,Shuling Xu,Yi Ding,Sixiu Sun

DOI: https://doi.org/10.1021/cg800288x

IF: 4.01

2008-01-01

Crystal Growth & Design

Abstract:Novel single-crystalline-like CeO2 hollow nanocubes were synthesized through a solvothermal method using peroxyacetic acid (PAA) as the oxidant in the absence of any templates. The structure and morphology of CeO2 hollow nanocubes were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS). The hollow nanocubes have an average edge length of 120 nm and shell thickness of 30 nm. TEM analyses demonstrate the formation of CeO2 hollow nanocubes is ascribed to the combination of oriented attachment and Ostwald ripening. At the beginning, a well-defined cube-like geometrical structure is formed through oriented attachment of small nanocrystallites. Then, solid evacuation in the central part via Ostwald ripening leads to single-crystalline-like hollow nanocubes. It was found that both peroxide (CH3COOOH or H2O2) and solution acidity are critical factors in determining the final morphology of the products. Compared to bulky CeO2 powders, the prepared CeO2 hollow nanocubes exhibited a higher catalytic activity toward CO oxidation.
One-Step Synthesis and Self-Assembly of Metal Oxide Nanoparticles into 3D Superlattices

Andrea Pucci,Marc-Georg Willinger,Feng Liu,Xiangbing Zeng,Valentina Rebuttini,Guylhaine Clavel,Xue Bai,Goran Ungar,Nicola Pinna

DOI: https://doi.org/10.1021/nn3010735

IF: 17.1

2012-01-01

ACS Nano

Abstract:A simple one-pot approach based on the "benzyl alcohol route" is introduced for the fabrication of highly ordered supercrystals composed of highly uniform 3-4 nm zirconia and rare-earth stabilized zirconia nanoparticles. The as-fabricated supercrystals reach sizes larger than 10 μm and present well-defined 3D morphologies such as flower-like, rhombic dodecahedron, and bipyramids. This system is unique in that the supercrystals are formed in one-step directly in the reaction medium where the nanoparticles are synthesized. The uniformity in nanocrystal shape and size is attributed to the in situ formation of benzoate species that directs the nanoparticle growth and assembly. The low colloidal stabilization of the benzoate-capped nanoparticles in benzyl alcohol promotes the formation of supercrystals in solution by π-π interaction between the in situ formed benzoate ligands attached to neighboring particles. By varying the reaction temperature and the nature of the doping the way the nanobulding blocks assemble in the supercrystals could be controlled. Standard FCC superlattice packings were found together with more unusual ones with P6/mmm and R ̅3m symmetries.
Facile Synthesis of Well-Defined CeO2 Hollow Spheres with a Tunable Pore Structure

Jian Zhang,Ming Gong,Chuanjin Tian,Chang-An Wang

DOI: https://doi.org/10.1016/j.ceramint.2015.12.166

IF: 5.532

2016-01-01

Ceramics International

Abstract:Herein, SiO2@CeO2 composite microspheres were successfully prepared via a hydrothermal assisted layer-by-layer self-assembly method employing colloid SiO2 as the template, which was fabricated by a typical Stöber method. Monodispersed CeO2 hollow spheres with a narrow size distribution were achieved after etching colloid SiO2 templates through NaOH. The resultant samples were characterized by X-ray diffraction (XRD), Scanning electron microscope (SEM), Transmission electron microscopy (TEM), Fourier translation infrared spectroscopy (FT-IR), X-ray photoelectron spectrum (XPS), and Nitrogen adsorption–desorption isothermal. Specifically, the shell thickness and the mesoporous structure of the hollow sphere can be easily controlled by changing the concentration of cerium source.
Controlled Synthesis And Self-Assembly Of Ceo2 Nanocubes

Songwang Yang,Lian Gao

DOI: https://doi.org/10.1021/ja063359h

IF: 15

2006-01-01

Journal of the American Chemical Society

Abstract:CeO2 nanocubes (and nanorods) enclosed by six {200} planes with controlled sizes have been prepared through a facile one-pot method. The nanocubes have a strong tendency to assemble into 2D and 3D arrays with regular patterns on a substrate, which is probably driven by the dipole-dipole interaction of polar {200} planes. The possible formation mechanism of the nanocubes has been put forward as the oriented aggregation mediated precursor growth. It is possible to use the synthesized nanocubes as building blocks to achieve {200}-perfect-oriented monolayers or thickness-controlled films and to apply the preparative method in the incorporation of heterogeneous atoms or nanoparticles for semiconductor doping or heterogeneous nanostructures.
Synthesis and characterisation of CeO2 nanoparticles and rods

Zhaoxia Zhang,Li Wang,Min Shao,Yili Guo,Guangliang Chen,Jianzhong Shao,Guoqing Zhang

DOI: https://doi.org/10.1049/mnl.2012.0406

2012-01-01

Abstract:Without adding any surfactant, CeO2 nanoparticles and nanorods are prepared by a very simple hydrothermal method. CeO2 nanocrystals with different morphologies were synthesised simply by dropping ammonia into cerium nitrate [Ce(NO3)3·6H2O] water solution at room temperature. The obtained samples were characterised by powder X-ray diffraction, scanning electron microscopy, transmission electron microscopy and UV-visible absorption spectroscopy. The results show that all samples are indexed to phase of CeO2. The synthesised nanoparticles are spherical with a 10-30-nm diameter and the nanorods are 100-200-nm in length and 5-10-nm in diameter. The morphology of CeO2 transforms from granular to rod-like with the ammonia concentration increasing from 0.5, 1 to 2 mol/l. The UV vis spectra exhibit a slight red shift because of increasing crystallite size.
Self-template hydrothermal synthesis of CeO2 hollow nanospheres

Genli Shen,Haidi Liu,Qi Wang,Zhen Wang,Yunfa Chen

DOI: https://doi.org/10.1007/s11051-012-0954-x

IF: 2.533

2012-06-01

Journal of Nanoparticle Research

Abstract:CeO2 hollow nanospheres were synthesized by a low-cost and environmentally benign one-pot hydrothermal route. Templates, surfactants, or other auxiliaries were not used in the route. X-ray diffraction, transmission electron microscopy, scanning electron microscopy, X-ray photoelectron spectroscopy, high-resolution transmission electron microscopy, and nitrogen adsorption–desorption measurements were used to characterize the products. The average diameter of hollow spheres, with shells of approximately 30 nm, was about 300 nm. The formation of these hollow spheres involved a transformation from Ce(OH)CO3 solid spheres to CeO2 hollow nanospheres. The CeO2 hollow nanospheres exhibited a higher catalytic activity on CO oxidation than CeO2 nano-octahedrons.

materials science, multidisciplinary,nanoscience & nanotechnology,chemistry
Spontaneous Organization of Uniform CeO2 Nanoflowers by 3D Oriented Attachment in Hot Surfactant Solutions Monitored with an in Situ Electrical Conductance Technique

Huan-Ping Zhou,Ya-Wen Zhang,Hao-Xin Mai,Xiao Sun,Qiang Liu,Wei-Guo Song,Chun-Hua Yan

DOI: https://doi.org/10.1002/chem.200701348

2008-01-01

Chemistry - A European Journal

Abstract:Uniform CeO(2) nanoflowers were synthesized by rapid thermolysis of (NH(4))(2)Ce(NO(3))(6) in oleic acid (OA)/oleylamine (OM), by a unique 3D oriented-attachment mechanism. CeO(2) nanoflowers with controlled shape (cubic, four-petaled, and starlike) and tunable size (10-40 nm) were obtained by adjusting the reaction conditions including solvent composition, precursor concentration, reaction temperature, and reaction time. The nanoflower growth mechanism was investigated by in situ electrical conductance measurements, transmission electron microscopy, and UV/Vis spectroscopy. The CeO(2) nanoflowers are likely formed in two major steps, that is, initial formation of ceria cluster particles capped with various ligands (e.g., OA, OM, and NO(3) (-)) via hydrolysis of (NH(4))(2)Ce(NO(3))(6) at temperatures in the range 140-220 degrees C, and subsequent spontaneous organization of the primary particles into nanoflowers by 3D oriented attachment, due to a rapid decrease in surface ligand coverage caused by sudden decomposition of the precursor at temperatures above 220 degrees C in a strong redox reaction. After calcination at 400 degrees C for 4 h the 33.8 nm CeO(2) nanoflowers have a specific surface area as large as 156 m(2) g(-1) with high porosity, and they are highly active for conversion of CO to CO(2) in the low temperature range of 200-400 degrees C. The present approach has also been extended to the preparation of other transition metal oxide (CoO, NiO, and CuO(x)) nanoflowers.
Mesoscale organization of nearly monodisperse flowerlike ceria microspheres.

Chunwen Sun,Jie Sun,Guoliang Xiao,Huairuo Zhang,Xinping Qiu,Hong Li,Liquan Chen

DOI: https://doi.org/10.1021/jp062179r

2006-01-01

Abstract:Nearly monodisperse flowerlike CeO2 microspheres were synthesized via a simultaneous polymerization-precipitate reaction, metamorphic reconstruction, and mineralization under hydrothermal condition as well as subsequent calcination. The obtained CeO2 microsphere consists of 20-30 nm thick nanosheets as petals. It has an open three-dimensional (3D) porous and hollow structure and possesses high surface area, large pore volume, and marked hydrothermal stability. It can be doped easily after synthesis, and the initial 3D texture is maintained. The controlling factors and a possible formation mechanism are discussed in detail. This novel material can be used as a support for catalysts with various purposes. With CuO loaded on flowerlike CeO2, the catalytic activities and hydrothermal stability of Cu/CeO2 for ethanol stream reforming were examined. At 300 degrees C, the H-2 selectivity reached a maximum value of 74.9 mol %, while CO was not detected within the precision of the gas chromatogram. It produced a hydrogen-rich gas mixture in the wide temperature range (300-500 degrees C) and showed excellent hydrothermal stability at high temperature (550 degrees C), which is a good choice for ethanol processors for hydrogen fuel cell applications.

One-pot Synthesis of Monodisperse CeO2 Nanocrystals and Superlattices

Solvothermal Synthesis, Electrochemical and Photocatalytic Properties of Monodispersed CeO2 Nanocubes

Facile Synthesis of Ceria Nanocrystals with Tuneable Size and Shape

Sustainable and Facile Route to Nearly Monodisperse Spherical Aggregates of CeO2 Nanocrystals with Ionic Liquids and Their Catalytic Activities for CO Oxidation

Preparation of CeO2 Nanocrystals by Solvothermal Routes

Controllable synthesis of nearly monodisperse spherical aggregates of CeO2 nanocrystals and their catalytic activity for HCHO oxidation.

One Step Hydrothermal Synthesis of CeO2–ZrO2 Nanocomposites and Investigation of the Morphological Evolution

A New Method to Preparing Monodisperse CeO_2 Nanoparticles

Wet chemical preparation of well-dispersed colloidal cerium oxide nanocrystals

Controlled Synthesis of CeO2 Nanoparticles from the Coupling Route of Homogenous Precipitation with Microemulsion

The Synthesis of Nanometer Sized CeO2 Particles by the Coupling Route of Microemulsion with Homogeneous Precipitation

General and facile synthesis of ceria-based solid solution nanocrystals and their catalytic properties

Mesoporous-shelled CeO2 hollow nanospheres synthesized by a one-pot hydrothermal route and their catalytic performance

Template-Free Synthesis Of Single-Crystalline-Like Ceo2 Hollow Nanocubes

One-Step Synthesis and Self-Assembly of Metal Oxide Nanoparticles into 3D Superlattices

Facile Synthesis of Well-Defined CeO2 Hollow Spheres with a Tunable Pore Structure

Controlled Synthesis And Self-Assembly Of Ceo2 Nanocubes

Synthesis and characterisation of CeO2 nanoparticles and rods

Self-template hydrothermal synthesis of CeO2 hollow nanospheres

Spontaneous Organization of Uniform CeO2 Nanoflowers by 3D Oriented Attachment in Hot Surfactant Solutions Monitored with an in Situ Electrical Conductance Technique

Mesoscale organization of nearly monodisperse flowerlike ceria microspheres.