Abstract:We report here a generalized synthesis of various crystalline mesoporous metal oxides including CeO2, Cr2O3, Fe2O3, SnO2, Ce0.5Zr0.5O2, TiO2, Al2O3 and ZrO2 from the self-assembly of a basic poly 4-vinylpyridine (P4VP) template with various metal precursors based on their strong acid–base interaction under high temperature (180 °C) hydrothermal conditions. Using the typically crystalline mesoporous metal oxide of CeO2, after removing the template by calcination at 550 °C and loading with various transition metal oxides such as MnOx, various transition metal oxide functionalized crystalline mesoporous CeO2 (MnOx/P4VP–CeO2) were obtained. X-ray diffraction (XRD) patterns show that the resulting mesoporous metal oxides exhibit a high degree of crystallinity, and the transition metal oxides active sites have been successfully loaded into these samples. N2 sorption–desorption isotherms, SEM images show that the resulting crystalline mesoporous metal oxides, such as CeO2, have a large BET surface area (94 m2 g−1) and abundant mesopores, which exhibit monolithic morphology with crystal sizes ranging from 5 to 15 μm, giving a uniform pore size centered at 5 nm. XPS spectra show that the active sites such as MnOx exhibit the phases of MnO2 and Mn2O3 in P4VP–CeO2. H2-TPR curves show that MnOx/P4VP–CeO2 exhibits decreased reductive temperatures of both active sites of the MnOx and P4VP–CeO2 supporter when compared with the samples reported previously. More importantly, MnOx/P4VP–CeO2 exhibits much better catalytic activities and good recyclability for catalyzing the oxidation of benzene than that of MnOx loaded commercially crystalline CeO2, which will be very important for their wide applications for VOCs removal in industry.

A Mild Solution Strategy for the Synthesis of Mesoporous Ceo2 Nanoflowers Derived from Ce(Hcoo)(3)

Spontaneous Organization of Uniform CeO2 Nanoflowers by 3D Oriented Attachment in Hot Surfactant Solutions Monitored with an in Situ Electrical Conductance Technique

Mesoscale organization of nearly monodisperse flowerlike ceria microspheres.

Sustainable and Facile Route to Nearly Monodisperse Spherical Aggregates of CeO2 Nanocrystals with Ionic Liquids and Their Catalytic Activities for CO Oxidation

Generalized and High Temperature Synthesis of a Series of Crystalline Mesoporous Metal Oxides Based Nanocomposites with Enhanced Catalytic Activities for Benzene Combustion

Mesoporous CeO2 nanobelts synthesized by a facile hydrothermal route via controlling cationic type and concentration of alkali

Mesoporous-shelled CeO2 hollow nanospheres synthesized by a one-pot hydrothermal route and their catalytic performance

Facile Synthesis of Well-Defined CeO2 Hollow Spheres with a Tunable Pore Structure

Facile Synthesis of Macrocellular Mesoporous Foamlike Ce-Sn Mixed Oxides with a Nanocrystalline Framework by Using Triblock Copolymer As the Single Template.

Controllable synthesis of nearly monodisperse spherical aggregates of CeO2 nanocrystals and their catalytic activity for HCHO oxidation.

Synthesis of CeO2 Hollow Nanospheres Via Redox Reaction Based Self-Templating Approach

Green synthesis and catalytic performance of nanoscale CeO2 sheets

Facile One-Step Synthesis of Double-Shelled CeO2 Hollow Spheres and Their Optical and Catalytic Properties

Co3O4/CeO2 Multi-Shelled Nanospheres Derived from Self-Templated Synthesis for Efficient Catalytic CO Oxidation.

Synthesis and characterisation of CeO2 nanoparticles and rods

Template-Free Synthesis Of Single-Crystalline-Like Ceo2 Hollow Nanocubes

A Facile Synthesis for Hierarchical Porous CeO2 Nanobundles and Their Superior Catalytic Performance for CO Oxidation

Catalytically Stable and Active CeO2 Mesoporous Spheres

Ultrafast, Continuous and Shape-Controlled Preparation of CeO2 Nanostructures: Nanorods and Nanocubes in a Microfluidic System

Facile Preparation Of Cu-Mn/Ceo2/Sba-15 Catalysts Using Ceria As An Auxiliary For Advanced Oxidation Processes

Facile synthesis of well-dispersed CeO2–CuOx composite hollow spheres with superior catalytic activity for CO oxidation