Abstract:Atomically dispersed metal catalysts often exhibit superior performance compared to that of nanoparticle catalysts in many catalysis processes. However, these so-called "single atom" catalysts have a consistently low loading density on the support surface and easily aggregate at high temperatures, hindering their practical application. Herein, we demonstrate a facile surface engineering protocol using molecule surface charge transfer adducts to fabricate highly stable noble metal catalysts with atomic dispersion, using a Pt/CeO2 catalyst as an example. The key of this approach is the generation of an adequate amount of Ce3+ defective sites on the porous CeO2 surface through the adsorption of reductive ascorbic acid molecules and a subsequent surface charge transfer process. Subsequently, noble metal Pt atoms can be well-dispersedly anchored onto the generated Ce3+ sites of porous CeO2 nanorods with a loading density of up to 1.0 wt %. The as-prepared highly dispersed Pt/CeO2 catalyst showed outstanding catalytic activity at near room temperature toward CO oxidation, with excellent stability over several days, which is far superior to the traditional impregnation-prepared catalysts, the activity (complete conversion at 90 degrees C) of which is severely decayed within a couple of hours. The proposed synthetic route is simple yet versatile and can therefore be potentially applied to fabricate other supported noble metal catalysts with atomic dispersion.

Catalytically Stable and Active CeO2 Mesoporous Spheres

Mesoporous-shelled CeO2 hollow nanospheres synthesized by a one-pot hydrothermal route and their catalytic performance

The Rational Design of Sandwich-Like MnO2-Pd-CeO2 Hollow Spheres with Enhanced Activity and Stability for CO Oxidation

Sustainable and Facile Route to Nearly Monodisperse Spherical Aggregates of CeO2 Nanocrystals with Ionic Liquids and Their Catalytic Activities for CO Oxidation

Facile synthesis of well-dispersed CeO2–CuOx composite hollow spheres with superior catalytic activity for CO oxidation

Surfactant-Mediated One-Pot Method to Prepare Pd–CeO2 Colloidal Assembled Spheres and Their Enhanced Catalytic Performance for CO Oxidation

Cu-doped CeO 2 spheres: Synthesis, characterization, and catalytic activity

Constructing Efficient CuO-Based CO Oxidation Catalysts with Large Specific Surface Area Mesoporous CeO2 Nanosphere Support

Facile One-Step Synthesis of Double-Shelled CeO2 Hollow Spheres and Their Optical and Catalytic Properties

Mesoporous MnCeOx Solid Solutions for Low Temperature and Selective Oxidation of Hydrocarbons.

Facile Synthesis Of 3d Flowerlike Ceo2 Microspheres Under Mild Condition With High Catalytic Performance For Co Oxidation

Design and Preparation of MnO2/CeO2-MnO2 Double-Shelled Binary Oxide hollow spheres and Their application in CO oxidation.

Pt-embedded-CeO2 hollow spheres for enhancing CO oxidation performance

High-Performance Znco2o4@Ceo2 Core Shell Microspheres for Catalytic Co Oxidation

Co3O4/CeO2 Multi-Shelled Nanospheres Derived from Self-Templated Synthesis for Efficient Catalytic CO Oxidation.

Surface Engineering Protocol to Obtain an Atomically Dispersed Pt/CeO2 Catalyst with High Activity and Stability for CO Oxidation

Facile Synthesis of Multi-Shelled Hollow Cu CeO2 Microspheres with Promoted Catalytic Performance for Preferential Oxidation of CO

Facile Synthesis of Highly Active Mesoporous PdCeOx Solid Solution for Low-Temperature CO Oxidation

Pt-embedded-CeO<sub>2</sub>hollow spheres for enhancing CO oxidation performance

Fabrication of High-performance CeO2-MnOx/TiO2/Ti Monolithic Catalysts for Low-temperature and Stable CO Oxidation

Transition-Metal Doped Ceria Microspheres with Nanoporous Structures for CO Oxidation