Facile Synthesis and Characterization of Ultrathin Cerium Oxide Nanorods

Yefeng Yang,Yizheng Jin,Haiping He,Zhizhen Ye

DOI: https://doi.org/10.1039/c004270f

IF: 3.756

2010-01-01

CrystEngComm

Abstract:Single-crystalline ultrathin nanorods of CeO2 with uniform diameters of ca. 1.5 nm have been synthesized via an oriented attachment process based on a facile solution-based approach.

What problem does this paper attempt to address?

Synthesis and characterization of ultrathin single-crystalline cerium oxide nanorods

yefeng yang,yizheng jin,zhizhen ye,yao tu,qinglmg wang

DOI: https://doi.org/10.1109/INEC.2010.5425007

2010-01-01

Abstract:We report a facile solution-based synthetic route to high-quality ultrathin cerium oxide nanorods with diameters of ~1.3 nm. High resolution transmission electron microscopy studies revealed that the nanorods were single-crystalline and grew along the [100] direction. The powder X-ray diffraction pattern of the final products indicated a cubic fluorite structure. The optical properties of the cerium oxide nanorods were explored by UV/Vis absorption and photoluminescence (PL) measurements at room temperature. The absorption edge of the ultrathin nanorods was obviously blue-shifted with respect to that of the bulk, suggesting the presence of size confinement resulted from the molecular-scale dimension of the nanorods. The current work is of interest for developing UV blocking and shielding materials, and would open up new opportunities for fundamental studies in the field of ultrathin nanorods and nanowires.
Ligand-Free Self-Assembly Of Ceria Nanocrystals Into Nanorods By Oriented Attachment At Low Temperature

Ning Du,Hui Zhang,Bingdi Chen,Xiangyang Ma,Deren Yang

DOI: https://doi.org/10.1021/jp074011r

2007-01-01

Abstract:Single-crystalline ceria nanorods have been fabricated by self-assembly of ceria nanocrystals via a simple, low-temperature, and ligand-free approach. Detailed high-resolution transmission electron microscopy shows that the nanorods are formed along the [211] or [110] direction by self-organization of truncated octahedral ceria nanocrystals, sharing the {111} or {200} planes with each other, whereas the previous report shows that only the [110] direction exists in ceria nanorods. The nucleation temperature and molar ratio of Ce3+ and OH- also play key roles in the formation of ceria nanorods. Moreover, the formation mechanism was explained in detail.
Growth Mechanism of Ceria Nanorods by Precipitation at Room Temperature and Morphology-Dependent Photocatalytic Performance

Zhao Liu,Xiaojing Li,Mohannad Mayyas,Pramod Koshy,Judy N. Hart,Charles C. Sorrell

DOI: https://doi.org/10.1039/c7ce00922d

IF: 3.756

2017-01-01

CrystEngComm

Abstract:Ceria (CeO2) nanorods have been prepared by simple short-term precipitation at room temperature for the first time.
Entanglement of CeO2 Nanorods and Graphene Nanoribbons and Their Properties Studies of Nanocomposites

Bo Zhang,Xiao Chun He,Ming Jun Gao,Xing Fa Ma,Guang Li

DOI: https://doi.org/10.4028/www.scientific.net/msf.814.153

2015-01-01

Materials Science Forum

Abstract:Nano/Micro-structured CeO2and their nanocomposites have been received considerable attention in basic research and commercial applications, such as, new energy fields, photocatalysts, environmental fields, et al. To extend its visible light response and pave the effective conductive channels for charge transfer and separation in nanoscale is still facing great challenges. To explore these key issues of materials chemistry and physics, CeO2nanorods were prepared with aid of soft templates by wet chemical approach. Graphene nanoribbons were obtained with unzipping method of carbon nanotube (CNTs). Entanglement of CeO2nanorods and graphene nanoribbons oxides was realized based on the supermolecular interactions between surface active groups of CeO2nanorods and graphene nanoribbons oxides and excellent flexibility of graphene nanoribbons. A series of characterizations were examined by SEM (scanning electron microscopy), TEM (transmission electron microscopy), XRD (X-ray diffraction), the Fourier-Transform Infrared (FTIR) spectra, ultraviolet-visible spectroscopy (UV-Vis) and so on. Photocatalytic efficiency was examined by selecting typical organic pollutants. The results indicated that the entanglement of a small amount of graphene nanoribbons on the surface of CeO2nanorods not only expanded the light response of nanocomposite to visible light, but also enhanced the adsorption properties to organic pollutants. Because of excellent charge transfer properties and high mobility of graphene nanoribbons, the nanocomposites of CeO2/graphene nanoribbons are favor for electron-holes pairs generated by visible light, separation, and transfer, which would be important potential applications in photocatalysts, artificial photosynthesis system, nano/micro-devices, et al.
Synthesis and characterisation of CeO2 nanoparticles and rods

Zhaoxia Zhang,Li Wang,Min Shao,Yili Guo,Guangliang Chen,Jianzhong Shao,Guoqing Zhang

DOI: https://doi.org/10.1049/mnl.2012.0406

2012-01-01

Abstract:Without adding any surfactant, CeO2 nanoparticles and nanorods are prepared by a very simple hydrothermal method. CeO2 nanocrystals with different morphologies were synthesised simply by dropping ammonia into cerium nitrate [Ce(NO3)3·6H2O] water solution at room temperature. The obtained samples were characterised by powder X-ray diffraction, scanning electron microscopy, transmission electron microscopy and UV-visible absorption spectroscopy. The results show that all samples are indexed to phase of CeO2. The synthesised nanoparticles are spherical with a 10-30-nm diameter and the nanorods are 100-200-nm in length and 5-10-nm in diameter. The morphology of CeO2 transforms from granular to rod-like with the ammonia concentration increasing from 0.5, 1 to 2 mol/l. The UV vis spectra exhibit a slight red shift because of increasing crystallite size.
Fine Control for the Preparation of Ceria Nanorods (111).

Changju Yang,Xiang Ning,Shanyong Chen,Xiaoxia Hou,Xiaoli Xia,Zhiyang Zhang,Weiping Ding,Luming Peng

DOI: https://doi.org/10.1039/d3ra02817h

IF: 4.036

2023-01-01

RSC Advances

Abstract:The synthesis of CeO2 nanorods with exposed (111) facets is optimized and the obtained material shows very narrow 17O NMR peaks, providing a foundation for future research on mechanisms using 17O solid-state NMR spectroscopy.
Fast Synthesis Of Cerium Oxide Nanoparticles And Nanorods

Feng Gao,Qingyi Lu,Sridhar Komarneni

DOI: https://doi.org/10.1166/jnn.2006.609

2006-01-01

Journal of Nanoscience and Nanotechnology

Abstract:The microwave-hydrothermal method has been investigated for the fast synthesis of rare earth cerium oxide (CeO(2)) nanoparticles and nanorods. This approach combines the advantages of both hydrothermal and microwave heating techniques. It is facile, rapid, energy-saving, and environmentally-benign and leads to high-yields. The average sizes of the obtained CeO(2) nanoparticles could be adjusted from similar to 1.6 nm to similar to 20 nm. Moreover, by changing cerium source and adjusting the amount of the added ammonia water, CeO(2) nanorods could be synthesized under microwave-assisted conditions for the first time. No calcination process or surfactant is required in our experiments for both CeO(2) nanoparticles and nanorods. The ultraviolet and visible (UV-vis) spectra show the obvious size-dependence of the position of the absorbance peak. The Brunaur Emmett Teller (BET) nitrogen adsorption indicates that these nanoparticles and nanorods have high specific surface areas, which are needed for potential applications in many fields. Compared with conventional hydrothermal method, microwave-assisted hydrothermal method shows its advantages of rapidity, convenience and perhaps cost-effectiveness and could be extended to the synthesis of other nanoparticles and nanorods.
Ultrafast, Continuous and Shape-Controlled Preparation of CeO2 Nanostructures: Nanorods and Nanocubes in a Microfluidic System

Hongbao Yao,Yujun Wang,Yu Jing,Guangsheng Luo

DOI: https://doi.org/10.1021/acs.iecr.8b01298

2018-01-01

Industrial & Engineering Chemistry Research

Abstract:Ceria nanorods enclosed with {110}/{100} planes and ceria nanocubes with {100} planes have been successfully prepared using a homemade microfluidic system in a continuous, ultrafast and shape-controllable manner. Only 8 min of reaction time are needed rather than days to synthesize ceria nanostructures in the traditional batch hydrothermal method. During the synthesis, reaction temperatures and base concentration have been demonstrated as the key factors responsible for the shape evolution. Accordingly, a morphological phase diagram was determined. In addition, polyvinylpyrrolidone was introduced to realize the transformation from ceria nanorods to nanocubes under unfavorable hydrothermal conditions. Catalytic performance of different CeO2 architectures was also examined in decomposing hydrogen peroxide and a reactivity trend (nanoparticles < nanorods < nonocubes) was observed. This is assumed to be related with different surface oxygen vacancy amounts as a result of {110}/{100} preferential planes, as confirmed by X-ray photoelectron spectroscopy and Raman analyses as well as density functional theory (DFT+U) calculations.
Synthesis and Characterization of Nanoscaled Cerium (IV) Oxide Via a Solid‐State Mechanochemical Method

J Lu,ZZ Fang

DOI: https://doi.org/10.1111/j.1551-2916.2005.00829.x

IF: 4.186

2006-01-01

Journal of the American Ceramic Society

Abstract:Solid-state reactions have the potential for direct preparation of ceramic powders and offer a low-temperature and low-cost alternative to conventional techniques for production of oxide powders. This paper describes a simple and effective mechanochemical method based on solid-state reactions during ball milling for synthesis of nanoscaled ceria (CeO2) particles. By using an organic base instead of an inorganic base, metal-ion-free nanoscaled CeO2 can also be made. The effects of annealing temperature on particle sizes and lattice strain are investigated. The results show that the average particle sizes of the particles increases and the average crystal lattice distortion decreases with the annealing temperature. Transmission electron microscopy examinations demonstrate that the CeO2 particles synthesised by this method are near-spherical shaped.
Enhanced Catalytic Activity of Ceria Nanorods from Well-Defined Reactive Crystal Planes

KB Zhou,X Wang,XM Sun,Q Peng,YD Li

DOI: https://doi.org/10.1016/j.jcat.2004.11.004

IF: 7.3

2005-01-01

Journal of Catalysis

Abstract:The crystal plane of ceria plays an essential role in determining its catalytic oxidation properties. In this study, single-crystalline CeO2 nanorods with well-defined crystal planes have been synthesized by a facile solution-based hydrothermal method. HRTEM studies reveal that the predominantly exposed planes are the unusually reactive {001} and {110} in the CeO2 nanorods rather than the stable {111} in the irregular nanoparticles. Consequently, it is demonstrated that the CeO2 nanorods are more reactive for CO oxidation than their counterparts, irregular nanoparticles. The present results indicate that catalysts with well-defined reactive sites may be “designed” because of the recent development of morphology-controlled synthesis of nanostructured materials.
Planar-dependent oxygen vacancy concentrations in photocatalytic CeO2 nanoparticles

Zhao Liu,Xiaojing Li,Mohannad Mayyas,Pramod Koshy,Judy N. Hart,C. C. Sorrell

DOI: https://doi.org/10.1039/c7ce01634d

IF: 3.756

2018-01-01

CrystEngComm

Abstract:The present work reports the rapid preparation of CeO2 nanorods by surfactant-free precipitation for the first time, which initiates a strategy for the quantitative elucidation of the importance of the exposed crystallographic planes and the oxygen vacancy concentrations of different morphologies of nanoceria. These relations are revealed through comparison of the relative surface areas of the exposed crystallographic planes. The precipitation temperature was critical in that nanooctahedra formed at the three lower temperatures and nanorods formed at the highest. The key feature to differentiate the photocatalytic performance was the morphology that the nanorods exhibit similar to 200% superior performance compared to those of the nanooctahedra. The principal reason for this is the presence of exposed {110} planes in the nanorods, which are not present in nanoctahedra. This crystallographic dependence of the improved performance of the nanorods is attributed directly to the greater oxygen vacancy concentration for the calculated surface area of this morphology.
Shape-selective Synthesis and Oxygen Storage Behavior of Ceria Nanopolyhedra, Nanorods, and Nanocubes.

Hx Mai,Ld Sun,Yw Zhang,R Si,W Feng,Hp Zhang,Hc Liu,Ch Yan

DOI: https://doi.org/10.1021/jp055584b

IF: 3.466

2005-01-01

The Journal of Physical Chemistry B

Abstract:Single-crystalline and uniform nanopolyhedra, nanorods, and nanocubes of cubic CeO2 were selectively prepared by a hydrothermal method at temperatures in the range of 100-180 degrees C under different NaOH concentrations, using Ce(NO3)3 as the cerium source. According to high-resolution transmission electron microscopy, they have different exposed crystal planes: {111} and {100} for polyhedra, {110} and {100} for rods, and {100} for cubes. During the synthesis, the formation of hexagonal Ce(OH)3 intermediate species and their transformation into CeO2 at elevated temperature, together with the base concentration, have been demonstrated as the key factors responsible for the shape evolution. Oxygen storage capacity (OSC) measurements at 400 degrees C revealed that the oxygen storage takes place both at the surface and in the bulk for the as-obtained CeO2 nanorods and nanocubes, but is restricted at the surface for the nanopolyhedra just like the bulk one, because the {100}/{110}-dominated surface structures are more reactive for CO oxidation than the {111}-dominated one. This result suggests that high OSC materials might be designed and obtained by shape-selective synthetic strategy.
Synthesis and characterization of ceria nanoparticles by complex-precipitation route

Yanping Li,Xue Bian,Yang Liu,Wenyuan Wu,Gaofeng Fu

DOI: https://doi.org/10.1007/s12613-020-2126-9

2022-01-15

Abstract:Ceria (CeO2) nanoparticles were successfully synthesized via a simple complex-precipitation route that employs cerium chloride as cerium source and citric acid as precipitant. The elemental analysis results of carbon, hydrogen, oxygen, and cerium in the precursors were calculated, and the results revealed that the precursors were composed of Ce(OH)3, Ce(H2Cit)3, or CeCit. X-ray diffraction analysis showed that all ceria nanoparticles had a face-centered cubic structure. With the molar ratio of citric acid to Ce3+ (n) of 0.25 and pH of 5.5, the specific surface area of the sample reached the maximum value of 83.17 m2/g. Ceria nanoparticles were observed by scanning electron microscopy. Selected area electron diffraction patterns of several samples were obtained by transmission electron microscopy, and the crystal plane spacing of each low-exponent crystal plane was calculated. The ultraviolet (UV)—visible transmittance curve showed that ceria can absorb UV light and pass through visible light. Among all samples, the minimum average transmittance of ultraviolet radiation a (UVA) was 4.42%, and that of ultraviolet radiation b (UVB) was 1.56%.

materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing
Sonochemical Fabrication and Characterization of Ceria (CeO2) Nanowires

Hong-Liang Chen,Hai-Yang Zhu,Hui Wang,Lin Dong,Jun-Jie Zhu

DOI: https://doi.org/10.1166/jnn.2006.17922

2006-01-01

Journal of Nanoscience and Nanotechnology

Abstract:Ceria (CeO2) nanowires have been successfully synthesized by a sonochemical method in ambient air and alkali aqueous solution from CeO2 nanoparticles without using any templates. The results showed that both alkali concentration and ultrasonic irradiation played critical roles in the formation of the nanowires. The crystalline structure and dimensions of the nanowires were characterized by powder X-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM) and selected area electron diffraction (SAED). The UV-visible absorption spectrum result showed that the products had conspicuous shape-specific effect. Microstructural analysis in HRTEM revealed that the preferential growth direction of CeO2 nanowires was [110]. Moreover, the catalytic activity of Au/CeO2 using CeO2 nanowires as support for CO conversion was higher than that obtained using bulk CeO2 as support.
Green synthesis and catalytic performance of nanoscale CeO2 sheets

guoqing zhang,ju ao,yili guo,zhaoxia zhang,min shao,lina wang,lan zhou,jianzhong shao

DOI: https://doi.org/10.1039/c4ra01004c

IF: 4.036

2014-01-01

RSC Advances

Abstract:Nanoscale CeO2 sheets were synthesized by a facile and green hydrothermal precipitation method in a strong alkali solution. The experimental results indicate that without any surfactant and template, nanoscale CeO2 sheets can be successfully synthesized simply by adding cerium nitrate into ammonia at room temperature. The Rietveld refinement analysis demonstrates that the synthesized CeO2 sheets have more defect structures than nanoparticles and nanorods. The photocatalytic performance of the CeO2 sheets was also evaluated by decomposing an azo dye, methyl orange. Compared with nanoparticles and nanorods, the synthesized CeO2 nanosheets exhibit higher photocatalytic activity during the degradation.
Low temperature chemical reaction synthesis of single-crystalline Eu(OH)3 nanorods and their thermal conversion to Eu2O3 nanorods

Ning Du,Hui Zhang,Bingdi Chen,Jianbo Wu,Dongsheng Li,Deren Yang

DOI: https://doi.org/10.1088/0957-4484/18/6/065605

IF: 3.5

2007-01-01

Nanotechnology

Abstract:We have developed a novel and simple method for chemical reaction synthesis of Eu(OH)(3) nanorods with a diameter of 20 - 30 nm and a length of about 300 nm at 90 degrees C using cyclohexylamine as the alkaline source instead of NaOH with subsequent thermal conversion to Eu2O3 nanorods at 700 degrees C. The effect of different alkaline sources on the shape of Eu(OH)(3) nanostructures has been investigated. Moreover, the morphology, structure and optical properties of the Eu(OH)(3) and Eu2O3 nanostructures prepared under different conditions have been characterized by transmission electron microscopy (TEM), field emission scanning electron microscopy (FESEM), x-ray powder diffraction (XRD), high-resolution transmission electron microscopy (HRTEM) and photoluminescence (PL). The mechanisms of formation for the synthesis of the Eu(OH)(3) nanostructures with different morphologies are presented.
General and facile synthesis of ceria-based solid solution nanocrystals and their catalytic properties

Huan-Ping Zhou,Rui Si,Wei-Guo Song,Chun-Hua Yan

DOI: https://doi.org/10.1016/j.jssc.2009.07.002

IF: 3.3

2009-01-01

Journal of Solid State Chemistry

Abstract:Uniform Ce1−xZrxO2 (x=0.2–0.8) nanocrystals with ultra-small size were synthesized through a thermolysis process, facilitated by the initial formation of precursor (hydrated (Ce,Zr)-hydroxides) at low temperature. TEM, XRD, EDAX, and Raman spectra were employed to study the formation of the solid solutions with various Ce/Zr ratios. Ultraviolet–visible (UV–vis) spectra showed that the ratios of Ce3+ to Ce4+ in both surface and bulk for the as-prepared Ce1−xZrxO2 nanocrystals increased with the zirconium content x. The well-distributed Zr and Ce in the hydrated (Ce,Zr)-hydroxides before their thermolysis became the crucial factor for the structural homogeneity of the products. In addition, this strategy was extended to the synthesis of Ce1−xGdxO1−x/2, Ce1−xSmxO1−x/2, and Ce1−xSnxO2 solid solutions. Catalytic measurements indicated that the ceria-based catalysts were active for CO oxidation at temperatures beyond 250°C and the sequence of catalytic activity was Ce0.5Zr0.5O2>Ce0.8Zr0.2O2>Ce0.2Zr0.8O2>Ce0.5Sm0.5O1.75.
A Facile Template-Free Synthesis of Praseodymium-Doped Ceria Nanorods

Ren Yaoyu,Deng Changsheng,Ai Desheng,Ma Jingtao,Zan Qingfeng,Kong Jiangrong,Xu Jingming

DOI: https://doi.org/10.4028/www.scientific.net/kem.434-435.714

2010-01-01

Key Engineering Materials

Abstract:Pr-doped ceria solid solutions have attracted much attention as promising mixed electronic-ionic conductor and oxygen storage materials. However, little effort has been made to synthesize Pr-doped ceria with one-dimensional nanostructure. In this paper, Pr-doped ceria nanorods were prepared via a facile hydrothermal method using Pr(NO3)3, Ce(NO3)3 and NaOH as raw materials. X-ray diffraction (XRD), transmission electron microscopy (TEM) and selected-area electron diffraction (SAED) indicated that the as-prepared Pr-doped ceria nanorods had a cubic fluorite structure, with the length around 200 ~ 400 nm and the diameters around 10 ~ 18 nm. The effect of alkaline concentration has been systematically studied and the results indicated that higher alkaline concentration was favorable for the formation of nanorods.
Preparation and Characterization of CeO2 with Different Particle Sizes and Morphology

Lai Jun Wang,Di Yang,Ming Wen,Ch.L. Song,Jian Chen,Yang Gu

DOI: https://doi.org/10.4028/www.scientific.net/ssp.121-123.21

2007-01-01

Abstract:The traditional precipitation method and a novel inorganic-organic hybrid method were used to control the morphology of nanocrystalline CeO2. By adjusting the methods and the preparation conditions, spherical and rode-shaped cerium dioxides with the nanoparticle sizes were prepared. Their structures and properties were characterized by XRD, BET and TEM.
Hydrothermal Synthesis of CeO2nanorods Using a Strong Base–weak Acid Salt As the Precipitant

Xiaobin Yin,Youjin Zhang,Zhiyong Fang,Zhenyu Xu,Wei Zhu

DOI: https://doi.org/10.1080/17458080.2010.515252

2012-01-01

Nanoscience Methods

Abstract:Single-crystalline CeO2 nanorods of the size of about 30 nm diameter and 300 nm length were synthesised by using a strong base–weak acid salt as the precipitant, by a simple hydrothermal method without any surfactant. The structure and properties of the CeO2 nanorods were characterised by X-ray diffraction, X-ray photoelectron spectroscopy, high-resolution transmission electron microscopy, selected-area electron diffraction, UV–visible absorption and scanning electron microscopy field emission. Reaction parameters, such as the reaction temperature, the reaction time, the molar ratio of the reactants and the pH value, were investigated by a series of control experiments. The effect of the strong base–weak acid salt in the synthesis of the CeO2 nanorods was discussed.

Facile Synthesis and Characterization of Ultrathin Cerium Oxide Nanorods

Synthesis and characterization of ultrathin single-crystalline cerium oxide nanorods

Ligand-Free Self-Assembly Of Ceria Nanocrystals Into Nanorods By Oriented Attachment At Low Temperature

Growth Mechanism of Ceria Nanorods by Precipitation at Room Temperature and Morphology-Dependent Photocatalytic Performance

Entanglement of CeO2 Nanorods and Graphene Nanoribbons and Their Properties Studies of Nanocomposites

Synthesis and characterisation of CeO2 nanoparticles and rods

Fine Control for the Preparation of Ceria Nanorods (111).

Fast Synthesis Of Cerium Oxide Nanoparticles And Nanorods

Ultrafast, Continuous and Shape-Controlled Preparation of CeO2 Nanostructures: Nanorods and Nanocubes in a Microfluidic System

Synthesis and Characterization of Nanoscaled Cerium (IV) Oxide Via a Solid‐State Mechanochemical Method

Enhanced Catalytic Activity of Ceria Nanorods from Well-Defined Reactive Crystal Planes

Planar-dependent oxygen vacancy concentrations in photocatalytic CeO2 nanoparticles

Shape-selective Synthesis and Oxygen Storage Behavior of Ceria Nanopolyhedra, Nanorods, and Nanocubes.

Synthesis and characterization of ceria nanoparticles by complex-precipitation route

Sonochemical Fabrication and Characterization of Ceria (CeO<sub>2</sub>) Nanowires

Green synthesis and catalytic performance of nanoscale CeO2 sheets

Low temperature chemical reaction synthesis of single-crystalline Eu(OH)<sub>3</sub> nanorods and their thermal conversion to Eu<sub>2</sub>O<sub>3</sub> nanorods

General and facile synthesis of ceria-based solid solution nanocrystals and their catalytic properties

A Facile Template-Free Synthesis of Praseodymium-Doped Ceria Nanorods

Preparation and Characterization of CeO<sub>2</sub> with Different Particle Sizes and Morphology

Hydrothermal Synthesis of CeO2nanorods Using a Strong Base–weak Acid Salt As the Precipitant

Facile Synthesis and Characterization of Ultrathin Cerium Oxide Nanorods

Synthesis and characterization of ultrathin single-crystalline cerium oxide nanorods

Ligand-Free Self-Assembly Of Ceria Nanocrystals Into Nanorods By Oriented Attachment At Low Temperature

Growth Mechanism of Ceria Nanorods by Precipitation at Room Temperature and Morphology-Dependent Photocatalytic Performance

Entanglement of CeO2 Nanorods and Graphene Nanoribbons and Their Properties Studies of Nanocomposites

Synthesis and characterisation of CeO2 nanoparticles and rods

Fine Control for the Preparation of Ceria Nanorods (111).

Fast Synthesis Of Cerium Oxide Nanoparticles And Nanorods

Ultrafast, Continuous and Shape-Controlled Preparation of CeO2 Nanostructures: Nanorods and Nanocubes in a Microfluidic System

Synthesis and Characterization of Nanoscaled Cerium (IV) Oxide Via a Solid‐State Mechanochemical Method

Enhanced Catalytic Activity of Ceria Nanorods from Well-Defined Reactive Crystal Planes

Planar-dependent oxygen vacancy concentrations in photocatalytic CeO2 nanoparticles

Shape-selective Synthesis and Oxygen Storage Behavior of Ceria Nanopolyhedra, Nanorods, and Nanocubes.

Synthesis and characterization of ceria nanoparticles by complex-precipitation route

Sonochemical Fabrication and Characterization of Ceria (CeO<sub>2</sub>) Nanowires

Green synthesis and catalytic performance of nanoscale CeO2 sheets

Low temperature chemical reaction synthesis of single-crystalline Eu(OH)<sub>3</sub> nanorods and their thermal conversion to Eu<sub>2</sub>O<sub>3</sub> nanorods

General and facile synthesis of ceria-based solid solution nanocrystals and their catalytic properties

A Facile Template-Free Synthesis of Praseodymium-Doped Ceria Nanorods

Preparation and Characterization of CeO&lt;sub&gt;2&lt;/sub&gt; with Different Particle Sizes and Morphology

Hydrothermal Synthesis of CeO2nanorods Using a Strong Base–weak Acid Salt As the Precipitant

Preparation and Characterization of CeO<sub>2</sub> with Different Particle Sizes and Morphology