Abstract:A graded anode-supported solid oxide fuel cell (SOFC) with the structure porous Ni-yttria stabilized zirconia (Ni-YSZ)vertical bar microporous Ni-YSZ vertical bar YSZ vertical bar La0.8Sr0.2MnO3 (LSM) was fabricated by a trilayer co-pressing-sintering method, and coating with an LSM cathode. Cu-CeO2 was impregnated into the porous Ni-YSZ layer using nitrate/glycol precursors to act as an anti-carbon catalyst to fabricate a graded Cu-CeO2-NiO-YSZ composite anode. The current-voltage (I-V), current-power (I-P), and long-term stability of the SOFC were tested using CH4 or H-2 as fuels and air as an oxidant. The results show that the co-pressing-sintering layers possess a gradient pore structure with defect-free combination. The power density of SOFC supported by a graded Ni-YSZ anode is 284 mW.cm(-2), operated at 850 degrees C using H-2 as a fuel, but decreases to 143 mW.cm(-2) when the fuel is changed to CH4. In contrast, the cell supported by a Cu-CeO2-Ni-YSZ anode show the reverse behavior, increasing from 176 to 196 mW.cm(-2) when the fuel is changed from H-2 to CH4 at 850 degrees C. Under a 250 mA.cm(-2) load using CH4 as the fuel, the output of the cell with a graded Ni-YSZ anode fluctuats and the cell is blocked after 10 h. At this point, carbon particles or fibers are observed in the anode layer by scanning electron microscopy (SEM). Conversely, the cell with a Cu-CeO2-Ni-YSZ anode shows stable power output for 50 h or longer, and no carbon deposition was observed inside the anode.

Preparation and Characteristics of Anode-Supported Solid Oxide Fuel Cells by Wet Ceramic Powder Process

YSZ Thin Films Prepared by a Novel Powder Coating Process on Porous NiO-YSZ Cermet

Solid Oxide Fuel Cells with Dense Yttria-Stabilized Zirconia Electrolyte Membranes Fabricated by a Dry Pressing Process

Fabrication and Properties of Anode-Supported Solid Oxide Fuel Cell

Fabrication and Performance Test of Solid Oxide Fuel Cells with Screen-Printed Yttria-Stabilized Zirconia Electrolyte Membranes

A Symmetrical Solid Oxide Fuel Cell Prepared by Dry-Pressing and Impregnating Methods

Anode-supported Solid Oxide Fuel Cell Based on Dense Electrolyte Membrane Fabricated by Filter-Coating

Thin Yttria-Stabilized Zirconia Electrolyte and Transition Layers Fabricated by Particle Suspension Spray

High Performance Solid Oxide Fuel Cells Based on Tri-Layer Yttria-Stabilized Zirconia by Low Temperature Sintering Process

Performance of Anode-Supported Single-Chamber Solid Oxide Fuel Cells

A cost-effective process for fabrication of metal-supported solid oxide fuel cells

Preparation of Yttria Stabilized Zirconia Powders with a Glycine-Nitrate Process for Intermediate-Temperature Solid Oxide Fuel Cells

FABRICATION AND PERFORMANCE OF WHOLE MEMBRANE -COMPONENT MICRO SOLID OXIDE FUEL CELL ON SOLID POROUS SUPPORT

Fabrication and Evaluation of a Ni/La0.75Sr0.25Cr0.5Fe0.5O3−δ Co-Impregnated Yttria-Stabilized Zirconia Anode for Single-Chamber Solid Oxide Fuel Cells

Preparation and Properties of Direct-Methane Solid Oxide Fuel Cell Based on a Graded Cu-CeO<sub>2</sub>-Ni-YSZ Composite Anode

Micro-Tubular Solid Oxide Fuel Cell with Asymmetric Structure Anode and La0.6Sr0.4Co0.8Cu0.2O3−δ Perovskite Cathode

Fabrication of an Anode-Supported Yttria-Stabilized Zirconia Thin Film for Solid-Oxide Fuel Cells Via Wet Powder Spraying

Fabrication and Performance of Anode-Supported Electrolyte Thin Films SOFCs

Preparation and Performance of Tri-layer Composite Anode Supported Fuel Cell

Preparation of YSZ thin films for intermediate temperature solid oxide fuel cells by dip-coating method

Metal-supported Solid Oxide Fuel Cells with In-Situ Sintered (bi2o3)0.7(er2o3)0.3–ag Composite Cathode