Abstract:For development of thin bioactive coatings on metal implants, a dense and uniform apatite layer was coated onto titanium (Ti) implants in situ by using a new biomimetic method, which is composed of apatite nucleation and growth steps in simulated body fluid (SBF). Analysis of the coatings by thin film X-ray diffraction and scanning electron microscopy-energy dispersive X-ray microanalysis (SEM-EMPA) before implantation showed that its characteristics were very similar to those of natural bone. The coated and uncoated rectangular plates were bilaterally implanted into the tibial proximal metaphyses of rabbits. After 6, 10 and 25 weeks post-implantation, the bone bonding and bone formation at the bone-implant interfaces were evaluated by a detachment test and undecalcified histological examination. Mechanical testing in tension showed that the failure load of apatite layer-coated Ti implants was significantly higher than that of uncoated control at each time period (all P < 0.001). Histologically, it was shown that bone was deposited directly onto the apatite coating without any intervening soft tissue, while in the paired controls, interpositional soft tissue was seen at the bone-implant interface. By SEM-EPMA, a uniform calcium- and phosphorus-rich layer was detected between the coated implants and bone, but not in uncoated controls at either earlier or later time periods. The results indicate that the apatite layer deposited on Ti in situ may significantly increase the bone bonding strength by providing a bioactive surface, which allows for an early bone apposition to the implant. In addition, the apatite layer-coated Ti produced by the biomimetic process may fulfil the requirements of favourable thin coatings and strong adhesion at the metal-coating interface.

Biomimetic Ca–P Coating on Pre-Calcified Ti Plates by Electrodeposition Method

Biomimetic Deposition of Apatite on Electrochemically Oxidized Titanium Substrates

[Experimental Study of Fast Formation of Biomimetic Apatite Coatings on Pure Titanium Surface].

[Fast Formation of Biomimetic Apatite Coatings on Pure Porous Titanium Implant's Surface].

Fabrication and in vitro evaluation of the collagen/hyaluronic acid PEM coating crosslinked with functionalized RGD peptide on titanium.

Calcium Phosphate Coating on AT Titanium Plate by CD and BD Methods

Preparation of Dicalcium Phosphate Anhydrous (Monetite) Biological Coating on Titanium by Spray-Drying Method

Apatite Layer-Coated Titanium for Use As Bone Bonding Implants

Carbonate apatite coating on titanium induced rapidly by precalcification.

Preparation and biological evaluation of Nano-HA coating on tatinium surfaces

BIOCERAMIC COATINGS ON TITANIUM SURFACES

Longer-Term Mechanical And Biological Evaluation Of Titanium Alloy Coated With Apatite Layer

Effect of pulsed electrodeposition time on the characteristics of calcium phosphates coating on TiO2 nanostructures

A simple biomimetic method for calcium phosphate coating

Biomimetic Calcium Phosphate Coatings for Bioactivation of Titanium Implant Surfaces: Methodological Approach and In Vitro Evaluation of Biocompatibility

Bioactive Composite Coating on Titanium Implants for Hard Tissue Repair

Hydrothermal growth of biomimetic calcium phosphate network structure on titanium surface for biomedical application

Bone Responses to Rough Titanium Implants Coated with Biomimetic Ca-P in Rabbit Tibia.

Biomimetic Coating of Compound Titania and Hydroxyapatite on Titanium

Research Review of Ca/P Bio-Ceramic Coatings Fabricated by Biomimetic Solution Method

BSA/HA Coating on Titanium Alloy for Direct Bond Formation