Abstract:For dental/orthopedic implants to achieve better bone apposition and bone-implant bonding, various approaches to improve titanium surfaces have been developed. Recently, a fluoridated hydroxyapatite (FHA) coating on titanium (Ti) implants was made by sol–gel method and shown to be a possible applicative bone implant. The purpose of the current study was to evaluate biological responses and biomechanical bonding strength of FHA coated Ti implants as compared with that of the conventional Ti alloys and hydroxyapatite (HA) coated Ti implants. In vitro assays were made using human osteoblast-like cell (MG63) culture on different implants with cell attachment, morphology and differentiation evaluations. The implant plates were also implanted into the proximal metaphysis of New Zealand White rabbit tibiae. After 8 and 16 weeks implantation, mechanical and histological assessments were performed to evaluate biomechanical and biological behavior in vivo. The results showed that the cell adhesion and cell growth rate on the FHA and HA surface was higher than that on cp Ti surface (p<0.01), and insignificant difference was observed between two coated groups. Mechanical test demonstrated that the FHA implants had a higher interface shear strength than the both controls at 8 and 16 wks, with no significant difference with HA-Ti. Histologically, the coated implants revealed a significantly greater percentage of bone-implant contact when compared with the uncoated implants. Results demonstrated that the new FHA surface improved cell adhesion and proliferation. The coating exhibited a bioactive mechanical and histological behavior at bone-implant interface, suggesting that a useful approach by combined coating processes could optimize implant surfaces for bone deposition and early implant fixation.

Calcium Phosphate Coating on AT Titanium Plate by CD and BD Methods

[Experimental Study of Fast Formation of Biomimetic Apatite Coatings on Pure Titanium Surface].

Longer-Term Mechanical And Biological Evaluation Of Titanium Alloy Coated With Apatite Layer

Apatite Layer-Coated Titanium for Use As Bone Bonding Implants

[Fast Formation of Biomimetic Apatite Coatings on Pure Porous Titanium Implant's Surface].

Biological Fabrication of Nacreous Coating on Titanium Dental Implant.

In Vivo Comparison of Bone Formation on Titanium Implant Surfaces Coated with Biomimetically Deposited Calcium Phosphate or Electrochemically Deposited Hydroxyapatite

Preparation of Dicalcium Phosphate Anhydrous (Monetite) Biological Coating on Titanium by Spray-Drying Method

In vivo and in vitro biological efficacy of double-layer coating of titanium with gelatin and calcium phosphate

Bioactive Composite Coating on Titanium Implants for Hard Tissue Repair

A simple biomimetic method for calcium phosphate coating

BIOCERAMIC COATINGS ON TITANIUM SURFACES

Bone Responses to Rough Titanium Implants Coated with Biomimetic Ca-P in Rabbit Tibia.

Preparation and biological evaluation of Nano-HA coating on tatinium surfaces

Biomimetic Calcium Phosphate Coatings for Bioactivation of Titanium Implant Surfaces: Methodological Approach and In Vitro Evaluation of Biocompatibility

Laminin Coating Promotes Calcium Phosphate Precipitation on Titanium Discs in vitro

Biomechanical comparison of biomimetically and electrochemically deposited hydroxyapatite-coated porous titanium implants.

Development of Bioactive Ceramic Coating on Titanium Alloy substrate for Biomedical Application Using Dip Coating Method

Biological and Biomechanical Behavior of Titanium Implants with Fluoridated Hydroxyapatite Coatings

Fabrication and in vitro evaluation of the collagen/hyaluronic acid PEM coating crosslinked with functionalized RGD peptide on titanium.

Carbonate apatite coating on titanium induced rapidly by precalcification.