Microstructural and Tribomechanical Characterization of NiB Coated 4150 Steel
Abhishek Soni,A. Kumaraswamy,B. Praveen Kumar
DOI: https://doi.org/10.1007/s11665-023-09068-w
IF: 2.3
2024-01-10
Journal of Materials Engineering and Performance
Abstract:This study presents a comprehensive investigation of electroless NiB coating (5 wt.% of B) as a potential alternative to Hard Chrome for gun barrel applications. Microstructural analysis via Scanning Electron Microscopy (SEM) revealed a densely packed cauliflower-type surface morphology in the NiB coating. Cross-sectional examinations exhibited wheat earring-like features with an average thickness of 30 μm. X-ray diffraction (XRD) analysis confirmed the presence of Ni 3 B, Ni 2 B, and Ni phases with an average crystallite size of 34 nm. Surface roughness and Berkovich nanoindentation studies were carried out to further characterize the coatings. Tribomechanical performance was evaluated through pin-on-disk tests performed at various temperatures (25, 300, 400, and 500 °C) using Oxygen-free Copper as the counter-disk, given its relevance in shell jackets. The tests involved loads ranging from 30 to 50 N, a sliding velocity of 2 m/s, and a constant sliding distance of 100 m. The mean friction coefficient of the NiB coating ranged from 0.15 to 0.65, while the specific wear rate, determined by weight loss during wear, ranged within (0.62-1.67) *10 −7 g N −1 m −1 . Micrographs of the worn NiB coated samples revealed mixed wear mechanisms, including abrasive, adhesive, fatigue, and oxidative wear mechanisms at room temperature, whereas oxidative wear predominated at elevated temperatures (300 °C).
materials science, multidisciplinary