Abstract:With the increase in service temperature of aero-engine hot components, the requirements for the high-temperature performance and processability of the powder metallurgy (PM) superalloys used for preparing turbine disks also increase. To overcome the bottlenecks that constrain the preparation and microstructure control of PM superalloys, this work investigates the impacts of hot compression parameters on the hot deformation behavior and microstructure evolution of a novel PM superalloy, FGH4113A. Hot compression tests were conducted on the FGH4113A alloy, which underwent hot isostatic pressing, within a temperature range of 1050 °C–1150 °C and at a consistent true strain rate ranging from 0.001s −1 to 1s −1 . The results reveal that the flow stress decreases progressively with the reduction of strain rate and the rise in temperature. Optimal hot deformation conditions are identified at a temperature of 1110 °C with strain rates ranging from 0.1s −1 to 1s −1 , and a temperature of 1130 °C with strain rates between 0.01s −1 and 0.1s −1 . Within these optimal regimes, grains are uniform, and the average grain size is maintained within10μm. Grain evolution during hot compression involves original grain deformation, followed by recrystallization, subsequent grain coarsening, and then deformation again. Additionally, the γ′ area fraction diminishes with an increase in deformation temperature. Specifically, as the deformation temperature raises from 1050 °C to 1110 °C, and subsequently to 1150 °C, at a rate of 0.001s −1 , the primary γ′ area fraction diminishes progressively from 6.2 % to 3.0 % and ultimately to zero. Above 1130 °C, the γ′ area fraction remained largely unaffected by variations in strain rate. These insights are pivotal, offering both experimental data and theoretical perspectives for optimal microstructure control in PM superalloys.

Correlation between microstructure and mechanical properties of novel Co-Ni-based powder metallurgy superalloy

Microstructures and Mechanical Properties of a L12-structured Precipitation Strengthened Co-based Superalloy

Study of Compression Fatigue Mechanism of Ni-Based Powder Metallurgy Superalloys

Influence of Co Content on the Microstructures and Mechanical Properties of a Ni–Co Base Superalloy Made by Specific Additive Manufacturing Process

Microstructure and Mechanical Properties of the As-Cast and Annealed CoNiV-based MEAs with Al Addition

The Effects of Co on the Microstructure and Mechanical Properties of Ni-Based Superalloys Prepared via Selective Laser Melting

Correlation between Microstructure and Mechanical Properties of Heat-Treated Novel Powder Metallurgy Superalloy

Mechanical properties and microstructural evolution of a novel (FeCoNi)86.93Al6.17Ti6.9 medium entropy alloy fabricated via powder metallurgy technique

Phase constitution, microstructure and mechanical properties of a Ni-based superalloy specially designed for additive manufacturing

Investigation of Microstructural Stability and Tensile Deformation Behavior of a Novel PM Ni-based Superalloy During Long-Term Thermal Exposure

Microstructure and Mechanical Properties of a Novel Powder Metallurgy Nickel-Base Superalloy

A Novel Forming Process for Powder Metallurgy of Superalloys

Effects of Ta/Nb/Ti Addition on the Microstructure and Mechanical Properties of Novel CoNi-based Superalloys Fabricated by Directed Energy Deposition

In-Situ Observations on the Fracture Mechanism of Diffusion-Alloyed Ni-Containing Powder Metal Steels and a Proposed Method for Tensile Strength Improvement

Tensile properties of three newly developed Ni-base powder metallurgy superalloys

Hot deformation behavior and microstructure evolution of a novel nickel-based powder metallurgy superalloy

Cu-Cr-Mg Alloy with Both High Strength and High Electrical Conductivity Manufactured by Powder Metallurgy Process

Microstructures and Mechanical Properties of a L1 2 -structured precipitation Strengthened Co-based Superalloy

Effect of Multiple Forging on Microstructure and Mechanical Properties of Powder Metallurgy Fgh4096 Superalloy

Microstructure evolution and reactive diffusion behavior of highly dense TiNi alloy prepared from Ti 2 Ni and TiNi 3 intermetallic compound powders

Microstructural Evolution and Defect Formation in a Powder Metallurgy Nickel-Based Superalloy Processed by Selective Laser Melting