Microstructure and Mechanical Properties of Novel Nickel-Based P/M Superalloy

Yang Jinlong,Long Anping,Xiong Jiangying,Zhang Gaoxiang,Guo Jianzheng

2022-01-01

Rare Metal Materials and Engineering

Abstract:The microstructure, tensile properties, strain-controlled low cycle fatigue properties and fracture morphology of a novel nickel-based powder metallurgy (P/M) superalloy (WZ-A3) were studied by SEM, OM, fatigue testing machine and tensile testing machine under different conditions. The results show that the previous particle boundary (PPB) formed during the hot isostatic pressing (HIP) process are fully eliminated by hot extrusion (HEX). With the increase of tensile temperature from room temperature to 800 degrees C, the tensile strength of the alloy decreases first (from room temperature to 400 degrees C), remains unchanged (from 400 to 550 degrees C), and then decreases (from 550 to 800 degrees C). At room temperature, the elongation of the HIP+HT samples are reduced by PPB. From 700 to 800 degrees C, these two states of the tensile fracture change from the mixed transgranular and intergranular fracture mode to the intergranular fracture mode. The fatigue life (N-f) of HIP+HEX+HT samples is higher than that of HIP+HT samples under small strain control (0.6%, 0.8%), which is related to the inclusions in the alloy. When the strain is large (1.0%, 1.2%, 1.4%), the N-f is close to each other. When the strain is 1.2%, the multiple platform-type fatigue crack sources appear in both samples.