Abstract:To date, the most commonly used aluminum alloys for additive manufacturing are eutectic/near-eutectic alloys. However, fabricating high strength aluminum parts has not yet been fully investigated due to solidification cracking and porosity formation, which make these alloys very hard to be processed. Electron beam selective melting (EBSM) of aluminum alloys has some advantages over selective laser melting. The process is not affected by reflectivity of aluminum powders, and parts exhibit less induced thermal stresses. In addition, oxidation is reduced due to vacuum condition. Therefore, the process provides high potential for the fabrication of aluminum alloys, specifically, Al2024 alloy which is widely used in different industries such as automotive and airline industries. Hence, these industries are highly benefitted from being able to build defect-free AM parts. This study is significant because Al2024 alloy is highly susceptible to solidification cracking and porosity formation, and crack-free samples with high relative densities have not been built by EBM process previously. The baseplate preheating temperature was set to 350 degrees C, and samples were fabricated by applying a proper powder bed preheating configuration for each layer. Different sets of processing parameters were used to investigate their effect on the performance of the parts. Archimedes technique was used to measure the relative density of samples, ranging from 95% to full-dense. The results showed that higher relative densities could be achieved by increasing the input energy to an optimum value; however, by further increasing the energy, the relative density decreases, which can be attributed to porosity formation. SEM and EBSD results showed equiaxed grains in a crack-free microstructure. Grain structure consisted of high angle grain boundaries having different crystallographic orientations with a few subgrains. Additionally, AlCuMnFe, AlCuMnFeSi, and eutectic Al2Cu phases were uniformly distributed in the alpha phase matrix. Microhardness results showed an almost uniform change of hardness values in both horizontal and vertical sections, ranging from 100 HV to 110 HV for as-built samples. Moreover, tensile and yield strengths of as-built samples reached 314 MPa and 191 MPa, respectively, which can be further increased by a proper post-processing treatment. (C) 2020 Elsevier B.V. All rights reserved.

Microstructure, mechanical properties and strengthening mechanisms of IN738LC alloy produced by Electron Beam Selective Melting

Microstructures and mechanical properties evolution of IN939 alloy during electron beam selective melting process

In-situ Study of Microstructure and Mechanical Properties of GH3536 Alloy Manufactured by Selective Laser Melting at 750 °C

Insight into Elongation and Strength Enhancement of Heat-Treated LPBF Ni-based Superalloy 718 Using In-Situ SEM-EBSD

Phase constitution, microstructure and mechanical properties of a Ni-based superalloy specially designed for additive manufacturing

Investigation of Microstructure and Mechanical Performance of IN738LC Superalloy Thin Wall Produced by Pulsed Plasma Arc Additive Manufacturing

Multiple Preheating Processes for Suppressing Liquefaction Cracks in IN738LC Superalloy Fabricated by Electron Beam Powder Bed Fusion (EB-PBF)

Selective laser melting of IN738 superalloy with a low Mn+Si content: Effect of energy input on characteristics of molten pool, metallurgical defects, microstructures and mechanical properties

Effect of heat treatments on the microstructure and mechanical properties of IN738LC prepared by electron beam powder bed fusion

High-temperature mechanical properties of nickel-based superalloys manufactured by additive manufacturing

Microstructures Of Components Synthesized Via Electron Beam Selective Melting Using Blended Pre-Alloyed Powders Of Ti6al4v And Ti45al7nb

Microstructure evolution of an Inconel 718 alloy prepared by electron beam smelting

Microstructure and Mechanical Properties of Novel Nickel-Based P/M Superalloy

Microstructural Characteristics and Mechanical Properties of an Additively Manufactured Nickel-Based Superalloy

High-temperature microstructure stability and fracture toughness of TiAl alloy prepared via electron beam smelting and selective electron beam melting

Ti-48Al-2Cr-2Nb alloys prepared by electron beam selective melting additive manufacturing: microstructural and tensile properties

Microstructure and Elevated Temperature Tensile Behaviour of Directionally Solidified Nickel Based Superalloy

Grain boundary network evolution in electron-beam powder bed fusion nickel-based superalloy Inconel 738

Selective electron beam melting of high strength Al2024 alloy; microstructural characterization and mechanical properties

Intermediate temperature creep and deformation behavior of a nickel-based superalloy prepared by electron beam layer solidification

Heterogeneous structures in a Ni-based superalloy with tailoring mechanical properties produced by a twin laser powder bed fusion system