Deposition of NiAl/Al3Ni2(CrB2) Coatings from Ni, Al and CrB2 Powders Using Mechanical Synthesis in Planetary Ball Mill

Maciej Szlezynger,Daniel Toboła,Jerzy Morgiel

DOI: https://doi.org/10.3390/ma17020492

IF: 3.4

2024-01-20

Materials

Abstract:Interest in composite thick coatings with an intermetallic matrix stimulates the development of new deposition techniques like the co-milling of pre-alloyed NiAl powder with platelet-shaped substrates. Obtained coatings were up to several micrometers thick as cold-welding of intermetallic particles was effective only at the start of this process, while later, chipping prevailed over added material. The present experiment covered the co-milling in the planetary ball mill of Ni and Al elemental powders (1:1 molar ratio) with AISI 304 steel platelets for 32 h at 300 rpm. Next, this process was repeated with an admixture of 15 wt.% of CrB2 powder. In both cases, their milling succeeded in producing up to a 200 μm coating after 4 h. The use of light, scanning and transmission electron microscopy (LM/SEM/TEM) helped to establish that the coatings had gradient microstructures with more refined crystallites of NiAl, Al3Ni2 and CrB2 closer to the surface. With the addition of a ceramic phase, the coatings presented higher hardness and lower friction during dry wear tests both at RT and at 500 °C.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper attempts to address the research related to the deposition of NiAl/Al₃Ni₂(CrB₂) coatings through mechanical synthesis in a planetary ball mill. Specifically, the study aims to explore the following points:

1. **Development of Deposition Techniques**: Currently available deposition techniques (such as atmospheric plasma spraying or detonation gun technology) can produce composite coatings that meet high adhesion and thickness requirements, but these coatings often have high porosity, leading to increased permeability to external environments. Therefore, new methods for manufacturing nanocrystalline composite coatings need to be developed.

2. **Application of Cold Welding Mechanism**: In the past, cold welding between metal powder particles and the ball and container walls during alloy mechanical synthesis was considered a phenomenon to be avoided. However, in recent years, this cold welding process has been viewed as a means of depositing various materials, including intermetallic compounds and composites. The study evaluates the potential of Ni and Al elemental powders and CrB₂ powder co-milled with a stainless steel substrate as a deposition coating.

3. **Enhancement of Coating Performance**: By adding a ceramic phase (CrB₂), the coating exhibits higher hardness and lower friction coefficient in dry friction tests, and shows excellent performance at both room temperature and 500°C.

In summary, the main objective of the paper is to explore the preparation process, microstructure, and mechanical properties of novel NiAl/Al₃Ni₂(CrB₂) coatings using mechanical synthesis methods, with the aim of obtaining composite coating materials with higher hardness, wear resistance, and corrosion resistance.