High-temperature oxidation and wear resistance of nano-ZrB 2 reinforced CoNiCrAlY composite coating via a step-fashion mechanical alloying powder process

Kang Yang,Guozheng Xu,Zitao Jiang,Yang Yang,Shihong Zhang,Shuoyu Wang,Zhenhang Ni

DOI: https://doi.org/10.1016/j.triboint.2023.108331

IF: 5.62

2023-02-13

Tribology International

Abstract:A nano-ZrB 2 reinforced CoNiCrAlY composite coating with highly dense structures was prepared by HVOF via a step-fashion mechanical alloying (MA) powder process. The microstructure, mechanical properties, high-temperature oxidation and wear resistance were analyzed. Results show that a high-quality CoNiCrAlY-ZrB 2 powder with expected powder size and homogenous dispersion of nano-ZrB 2 can be obtained by the 35 h step-fashion MA. The addition of nanoscale ZrB 2 greatly improves mechanical properties of CoNiCrAlY-ZrB 2 coating, while the low content β-NiAl phase hinders its oxidation performance. Due to the formation of "upper enamel layer" during sliding process and the excellent hardness/fracture toughness, the wear resistance of CoNiCrAlY-ZrB 2 coating (2.46×10 -14 m 3 ·N -1 ·m -1 ) at 1000 °C is much better than that of CoNiCrAlY coating (1.9×10 -12 m 3 ·N -1 ·m -1 ), showing that CoNiCrAlY-ZrB 2 coating has a high potential for protecting hot parts.

engineering, mechanical