Electron-Beam and Plasma Oxidation-Resistant and Thermal-Barrier Coatings Deposited on Turbine Blades Using Cast and Powder Ni(Co)CrALY(Si) Alloys I. Fundamentals of the Production Technology, Structure, and Phase Composition of Cast NiCrAlY Alloys

T.O. Prikhna,I.M. Grechanyuk,M.V. Karpets,M.I. Grechanyuk,G.A. Baglyuk,V.G Grechanyuk,V.O. Chornovol

DOI: https://doi.org/10.1007/s11106-022-00296-8

2022-09-24

Powder Metallurgy and Metal Ceramics

Abstract:The process of producing alloys with elements that are uniformly distributed throughout an ingot is described. The structural features of NiCrAlY alloys produced by electron-beam melting, excluding primary vacuum induction melting of the starting mixture, were studied. The MZP6 and MZP7 alloys, differing in aluminum content, were examined. The cast material produced from the MZP7 alloy contained the γ phase: a standard solid solution of chromium and aluminum in nickel. The β-NiAl phase was found to be the main phase in the MZP6 alloy. Chain and globular precipitates characteristic of the γ′ phase and a small number of α-Cr-based compounds of variable composition were identified as well. The γ′ phase was detected in the NiCrAlY alloys containing more than 5 wt.% Al. Standard microstructures of the cast ingots produced from the MZP7 and MZP6 alloys indicated that the structural elements refined when the aluminum content increased from 4–6 wt.% (MZP7) to 11–14 wt.% (MZP6), the amounts of nickel, chromium, and yttrium being equal. The MZP7 alloy was characterized by a smooth transition from a fine-grained structure in the areas adjacent to the cooled mold surfaces to a coarse-grained one, formed in the central ingot regions. This phenomenon was less pronounced for the MZP6 alloy ingots. The lattice parameters of the NiCrAlY alloys were determined with the Rietveld refinement of the X-ray diffraction patterns. Maps showing the distribution of elements in the NiCrAlY alloy were provided.

metallurgy & metallurgical engineering,materials science, ceramics