Abstract:In this paper, we discussed recent studies done in our laboratories with a floating catalyst chemical vapor deposition (CVD) method. We can grow single- or double-walled carbon nanotubes (SWNTs/DWNTs) with different kinds of catalysts. Single-walled carbon nanotubes without amorphous carbon coating were prepared by thermally decomposing acetylene (C2H2) at the temperature range of 750–1200°C with ferrocene as catalyst. While with sulfur promoted ferrocene catalyst, double-walled carbon nanotubes were mass-produced by pyrolizing C2H2 at the temperature range of 900–1100°C. Furthermore, tunable growth of DWNTs with different diameter was achieved in our experiment. It is found that DWNTs produced at lower carbon partial pressure have much smaller inner tubes, even DWNTs with the smallest inner diameter of 0.4nm was found in here. As convenient and effective tool, radial breathing mode (RBM) of Raman scattering technique can be used to distinguish SWNTs from DWNTs. In further studies of Raman scattering with DWNTs, the possible match of the inner tubes and the outer tubes according to the RBM bands was assigned, and different chirality types were discussed according to the diameter and chirality dependence of resonant Raman vibration. We also investigated the temperature-dependent frequency shift of resonant Raman spectra of DWNTs in the range of 78–650K. We found that different RBM peaks, which are relative to different tube diameters, have different temperature coefficient of frequency shift, and the larger diameter carbon nanotubes have more RBM frequency downshift with increasing temperature. It is ascribed to the RBM frequency variation to the temperature dependence of the stretching force constant of C–C bond. Besides, Polarized Raman spectra were preformed on well-aligned SWNTs structure fabricated through post-growth method and found that the angular dependence of Raman intensity is consistent well with the predictions of the resonance Raman theory.

Controllable growth of double wall carbon nanotubes in a floating catalytic system

Controllable growth of single wall carbon nanotubes by pyrolizing acetylene on the floating iron catalysts

Double wall carbon nanotubes promoted by sulfur in a floating iron catalyst CVD system

Preparation of Double-Walled Carbon Nanotubes

Controllable preparation and properties of single-/double-walled carbon nanotubes

Producing cleaner double-walled carbon nanotubes in a floating catalyst system

Selective growth of semiconducting single-walled carbon nanotubes solely from carbon monoxide

The confined growth of double-walled carbon nanotubes in porous catalysts by chemical vapor deposition

Raman Characterization and Tunable Growth of Double-Wall Carbon Nanotubes

Synthesis of Double-Walled Carbon Nanotubes by Floating Chemical Vapor Deposition Method in a Reactor with Varied Diameter

Growth of Single-Walled Carbon Nanotubes with Controlled Diameters and Lengths by an Aerosol Method

Growth of Single-Walled Carbon Nanotubes with Controlled Structure: Floating Carbide Solid Catalysts

A New Understanding of Carbon Nanotube Growth: Activation and Deactivation of a Catalyst

Controlled Growth of Single-Walled Carbon Nanotubes at Atmospheric Pressure by Catalytic Decomposition of Ethanol and an Efficient Purification Method

Precise control of the number of walls formed during carbon nanotube growth using chemical vapor deposition

A New Method for Synthesizing Double-Walled Carbon Nanotubes

Controlled Growth of Single-Walled Carbon Nanotubes by Catalytic Decomposition of CH4 over Mo/Co/MgO Catalysts

Producing Carbon Nanotube Powder in A Floating Iron Catalyst Lpcvd System

Double Wall Carbon Nanotubes with an Inner Diameter of 0.4 nm

Effect of Temperature, Pressure, and Gas Ratio of Methane to Hydrogen on the Synthesis of Double-Walled Carbon Nanotubes by Chemical Vapour Deposition

Preparation of highly pure double-walled carbon nanotubes