Abstract:In this paper, we discussed recent studies done in our laboratories with a floating catalyst chemical vapor deposition (CVD) method. We can grow single- or double-walled carbon nanotubes (SWNTs/DWNTs) with different kinds of catalysts. Single-walled carbon nanotubes without amorphous carbon coating were prepared by thermally decomposing acetylene (C2H2) at the temperature range of 750–1200°C with ferrocene as catalyst. While with sulfur promoted ferrocene catalyst, double-walled carbon nanotubes were mass-produced by pyrolizing C2H2 at the temperature range of 900–1100°C. Furthermore, tunable growth of DWNTs with different diameter was achieved in our experiment. It is found that DWNTs produced at lower carbon partial pressure have much smaller inner tubes, even DWNTs with the smallest inner diameter of 0.4nm was found in here. As convenient and effective tool, radial breathing mode (RBM) of Raman scattering technique can be used to distinguish SWNTs from DWNTs. In further studies of Raman scattering with DWNTs, the possible match of the inner tubes and the outer tubes according to the RBM bands was assigned, and different chirality types were discussed according to the diameter and chirality dependence of resonant Raman vibration. We also investigated the temperature-dependent frequency shift of resonant Raman spectra of DWNTs in the range of 78–650K. We found that different RBM peaks, which are relative to different tube diameters, have different temperature coefficient of frequency shift, and the larger diameter carbon nanotubes have more RBM frequency downshift with increasing temperature. It is ascribed to the RBM frequency variation to the temperature dependence of the stretching force constant of C–C bond. Besides, Polarized Raman spectra were preformed on well-aligned SWNTs structure fabricated through post-growth method and found that the angular dependence of Raman intensity is consistent well with the predictions of the resonance Raman theory.

Producing cleaner double-walled carbon nanotubes in a floating catalyst system

Water-Assisted Preparation of High-Purity Semiconducting (14,4) Carbon Nanotubes

Efficiently producing single-walled carbon nanotube rings and investigation of their field emission properties

Preparation of highly pure double-walled carbon nanotubes

Controllable growth of double wall carbon nanotubes in a floating catalytic system

Double wall carbon nanotubes promoted by sulfur in a floating iron catalyst CVD system

Preparation of Double-Walled Carbon Nanotubes

Controllable preparation and properties of single-/double-walled carbon nanotubes

Carburization of Fe/Ni Catalyst for Efficient Growth of Single-Walled Carbon Nanotubes

Synthesis of Single-Walled Carbon Nanotubes by the Vertical Floating Catalyst Method

The Improvement of Yield and Thermal Stability of Single-Walled Carbon Nanotubes Fabricated by Gd-Assisted FCCVD

Carbon fiber-promoted activation of catalyst for efficient growth of single-walled carbon nanotubes

Producing Carbon Nanotube Powder in A Floating Iron Catalyst Lpcvd System

Co-synthesis of Single-Walled Carbon Nanotubes and Carbon Fibers

Purifying Double-Walled Carbon Nanotubes by Vacuum High-Temperature Treatment

Controlled Growth of Single-Walled Carbon Nanotubes at Atmospheric Pressure by Catalytic Decomposition of Ethanol and an Efficient Purification Method

A New Method for Synthesizing Double-Walled Carbon Nanotubes

Controlling the Crystalline Quality and Yield of Single‐Walled Carbon Nanotubes via Floating Catalyst Chemical Vapor Deposition Synthesis

Preparation of carbon nanofibers by the floating catalyst method

Double Wall Carbon Nanotubes with an Inner Diameter of 0.4 nm

Synthesis of Double-Walled Carbon Nanotubes by Floating Chemical Vapor Deposition Method in a Reactor with Varied Diameter