Abstract:In this paper, we discussed recent studies done in our laboratories with a floating catalyst chemical vapor deposition (CVD) method. We can grow single- or double-walled carbon nanotubes (SWNTs/DWNTs) with different kinds of catalysts. Single-walled carbon nanotubes without amorphous carbon coating were prepared by thermally decomposing acetylene (C2H2) at the temperature range of 750–1200°C with ferrocene as catalyst. While with sulfur promoted ferrocene catalyst, double-walled carbon nanotubes were mass-produced by pyrolizing C2H2 at the temperature range of 900–1100°C. Furthermore, tunable growth of DWNTs with different diameter was achieved in our experiment. It is found that DWNTs produced at lower carbon partial pressure have much smaller inner tubes, even DWNTs with the smallest inner diameter of 0.4nm was found in here. As convenient and effective tool, radial breathing mode (RBM) of Raman scattering technique can be used to distinguish SWNTs from DWNTs. In further studies of Raman scattering with DWNTs, the possible match of the inner tubes and the outer tubes according to the RBM bands was assigned, and different chirality types were discussed according to the diameter and chirality dependence of resonant Raman vibration. We also investigated the temperature-dependent frequency shift of resonant Raman spectra of DWNTs in the range of 78–650K. We found that different RBM peaks, which are relative to different tube diameters, have different temperature coefficient of frequency shift, and the larger diameter carbon nanotubes have more RBM frequency downshift with increasing temperature. It is ascribed to the RBM frequency variation to the temperature dependence of the stretching force constant of C–C bond. Besides, Polarized Raman spectra were preformed on well-aligned SWNTs structure fabricated through post-growth method and found that the angular dependence of Raman intensity is consistent well with the predictions of the resonance Raman theory.

Double wall carbon nanotubes promoted by sulfur in a floating iron catalyst CVD system

Controllable growth of double wall carbon nanotubes in a floating catalytic system

Double Wall Carbon Nanotubes with an Inner Diameter of 0.4 nm

Synthesis of Double-Walled Carbon Nanotubes by Floating Chemical Vapor Deposition Method in a Reactor with Varied Diameter

Growth of double-walled carbon nanotubes from silicon oxide nanoparticles

Preparation of Double-Walled Carbon Nanotubes

Raman Characterization and Tunable Growth of Double-Wall Carbon Nanotubes

Preparation of highly pure double-walled carbon nanotubes

Producing cleaner double-walled carbon nanotubes in a floating catalyst system

Selective growth of semiconducting single-walled carbon nanotubes solely from carbon monoxide

Controllable preparation and properties of single-/double-walled carbon nanotubes

Controllable growth of single wall carbon nanotubes by pyrolizing acetylene on the floating iron catalysts

Producing Carbon Nanotube Powder in A Floating Iron Catalyst Lpcvd System

Influence of Cerium Metal As Catalyst on the Growth and Structure of Single-Walled Carbon Nanotubes

Thin-Film Metal Catalyst For The Production Of Multi-Wall And Single-Wall Carbon Nanotubes

CVD Growth of Carbon Nanotube Forest with Selective Wall-Number from Fe–Cu Catalyst

A New Method for Synthesizing Double-Walled Carbon Nanotubes

Growth of high-density single-wall carbon nanotubes with a uniform structure using a CoRu catalyst

Nucleation of Carbon-Sulfur Phases by Manipulation of Vertically-Aligned Mm-Long Films of Iron-Filled Few-Wall/multiwall Carbon Nanotubes

Selective Synthesis of Single/Double/Multi-walled Carbon Nanotubes on MgO-Supported Fe Catalyst

The confined growth of double-walled carbon nanotubes in porous catalysts by chemical vapor deposition