Abstract:Double-walled carbon nanotubes (DWCNTs) make up a unique class of carbon nanotubes (CNTs) that are particularly intriguing for scientific research and are promising candidates for technological applications. A more precise level of control and greater yields can be achieved via catalytic chemical vapor deposition (CCVD), which involves the breakdown of a carbonaceous gas over nanoparticles. The addition of molybdenum to the system can increase the selectivity with regard to the number of walls that exist in the obtained CNTs. As reported herein, we have designed and synthesized a novel Co-Mo-MOF, [Co(3-bpta)1.5(MoO4)]·H2O (where 3-bpta = N,N'-bis(3-pyridyl)terephthalamide), and employed the Co-Mo-MOF as a bimetallic catalyst precursor for the CCVD approach to prepare high-quality DWCNTs. The Co-Mo-MOF was employed after being calcined in N2 and H2 at 1100 °C and decomposing into CoO, CoMoO4, and MoO3. Existing CoMoO4 is unaltered after reduction in H2 at 1100 °C, while CoO and MoO3 are converted into Co0 and MoO2, and more CoMoO4 is created at the expense of Co0 and MoO2 without clearly defining agglomeration. Finally, the interaction between metallic Co particles and C2H4 is what initiates the formation of DWCNTs. In-depth discussion is provided in this paper regarding the mechanism underlying the high selectivity and activity of Co-Mo catalysts in regulating the development and structure of DWCNTs. The DWCNTs also offer excellence performance when they are used as water purification agents and as selective sorbents. This work opens a feasible way to use MOFs as a way to produce MWCNTs, thus blazing a new trail in the field of MOF-derived carbon-based materials.

The confined growth of double-walled carbon nanotubes in porous catalysts by chemical vapor deposition

Nanopore Structure of Highly Enriched Double-Walled Carbon Nanotube Network Assemblies

Growth and Characterization of Bamboo-Like Multiwalled Carbon Nanotubes over Cu/Al2o3 Catalyst

Effect of Temperature, Pressure, and Gas Ratio of Methane to Hydrogen on the Synthesis of Double-Walled Carbon Nanotubes by Chemical Vapour Deposition

Very High-Quality Single-Walled Carbon Nanotubes Grown Using a Structured and Tunable Porous Fe/MgO Catalyst

CO<sub>2</sub>-Assisted SWNT Growth on Porous Catalysts

Formation Mechanism of Carbon Encapsulated Fe Nanoparticles in the Growth of Single-/Double-walled Carbon Nanotubes

Controllable growth of double wall carbon nanotubes in a floating catalytic system

Growth of double-walled carbon nanotubes from silicon oxide nanoparticles

Synthesis of high-quality double-walled carbon nanotubes using porous MgO nanowire supported iron oxide as catalyst

Preparation of Double-Walled Carbon Nanotubes

A New Understanding of Carbon Nanotube Growth: Activation and Deactivation of a Catalyst

Influence of Catalyst Structures on Carbon Nanotubes Growth Via Methane-CVD

Catalytic Growth of Multi-Wall Carbon Nanotubes on Carbon Cloth Using Powdery Ferrous Sulfate Heptahydrate As Catalyst Precursor

The effect of phase separation in Fe/Mg/Al/O catalysts on the synthesis of DWCNTs from methane

Synthesis of High‐Quality, Double‐Walled Carbon Nanotubes in a Fluidized Bed Reactor

Carbon Nanotube Synthesis and Parametric Study Using CaCO3 Nanocrystals As Catalyst Support by CVD

Synthesis of Single-Walled Carbon Nanotubes with Narrow Diameter Distribution by Calcination of a Mo-Modified Fe/MgO Catalyst

Fabrication of a Co-Mo-Based Metal-Organic Framework for Growth of Double-Walled Carbon Nanotubes

Dispersion-Enhanced Supported Pd Catalysts for Efficient Growth of Carbon Nanotubes Through Chemical Vapor Deposition

Growth of High-Density Parallel Arrays of Ultralong Carbon Nanotubes with Catalysts Pinned by Silica Nanospheres