Abstract:We studied the growth of carbon nanotubes(CNTs) over a Co/Mo/Al_2O_3 catalyst by decomposing ethylene with or without the assistance of water.The optimal amount of water was determined to be 0.6%(φ) since excess water removed the amorphous carbon around the catalysts and also directly etched the CNTs at high temperature.Under this condition,the yield of CNTs can be increased from 3.7 g·g~(-1),based on the mass of catalyst,to 70 g·g~(-1) within 1 h.The time-dependent online conversion of ethylene and the ratio of effective catalysts suggested that the effect of water is insignificant in the final growth period of the CNTs compared to that at the beginning.The correlation between the relative activity of the catalyst and the relative density of the CNT agglomerate suggests that the lack of growth volume inside the CNT agglomerate results in a gradual deactivation of the catalyst in the final CNT growth period. Raman characterization suggests that the degree of CNT defects increases with the bulk density of the CNT agglomerates since the mechanical resistance that is exposed on CNTs inside the agglomerate increases with reaction time.Thermal-gravimetric analysis indicates that the purity of CNTs ranges from 95.0%to 99.9%for a product with average purity of 99.2%.The non-uniform purity of the CNTs is due to the difference in mechanical resistance inside and outside the CNT agglomerate.The growth of CNTs outside the agglomerate is nearly free of mechanical resistance compared to that inside the agglomerate and,consequently,results in a high yield and high purity for the CNTs.These results suggest that it is necessary to control the agglomerate size and the structure,and to use a reactor with a large reactor volume for the growth of CNTs with low resistance and with high yield.

CO<sub>2</sub>-Assisted SWNT Growth on Porous Catalysts

Enhanced Selective Hydrogenation of CO2 to CH4 on Molybdenum Carbide Hollow Sphere Catalyst

Oxygen-Assisted Synthesis of Swnts from Methane Decomposition

Controlled Growth of Single-Walled Carbon Nanotubes by Catalytic Decomposition of CH4 over Mo/Co/MgO Catalysts

The confined growth of double-walled carbon nanotubes in porous catalysts by chemical vapor deposition

Effect of CO_2 on the Structural Variation of Na_2WO_4/Mn/SiO_2 Catalyst for Oxidative Coupling of Methane to Ethylene

SiO2-promoted growth of single-walled carbon nanotubes on an alumina supported catalyst

Selective growth of semiconducting single-walled carbon nanotubes solely from carbon monoxide

Synthesis of Single-Walled Carbon Nanotubes with Narrow Diameter Distribution by Calcination of a Mo-Modified Fe/MgO Catalyst

Very High-Quality Single-Walled Carbon Nanotubes Grown Using a Structured and Tunable Porous Fe/MgO Catalyst

Carbon fiber-promoted activation of catalyst for efficient growth of single-walled carbon nanotubes

Water-Assisted Growth of Carbon Nanotubes over Co/Mo/Al_2O_3 Catalyst

Supported catalysts derived from cobalt phyllosilicates for chemical vapor deposition growth of single-walled carbon nanotubes

Effect of organic additives in catalyst preparation on the growth of single-wall carbon nanotubes prepared by catalyst-assisted chemical vapour deposition

Carburization of Fe/Ni Catalyst for Efficient Growth of Single-Walled Carbon Nanotubes

Large- Scale Production of Single- Walled Carbon Nanotubes Using Fe/Mo/MgO Cryogel Catalyst

Pii: s0008-6223(02)00175-6

Synthesis Of High Quality Single-Walled Carbon Nanotubes By Cvd And Effect Of Catalyst'S Acidity-Basicity On Nanotubes Growth

Possible Tactics to Improve the Growth of Single-Walled Carbon Nanotubes by Chemical Vapor Deposition

Single wall carbon nanotubes growth over cobalt-iron mesoporous MCM-41 bimetallic catalyst under methane chemical vapor deposition, an experimental and DFT evaluation

Iron promoted MOF-derived carbon encapsulated NiFe alloy nanoparticles core-shell catalyst for CO2 methanation