Abstract:We studied the growth of carbon nanotubes(CNTs) over a Co/Mo/Al_2O_3 catalyst by decomposing ethylene with or without the assistance of water.The optimal amount of water was determined to be 0.6%(φ) since excess water removed the amorphous carbon around the catalysts and also directly etched the CNTs at high temperature.Under this condition,the yield of CNTs can be increased from 3.7 g·g~(-1),based on the mass of catalyst,to 70 g·g~(-1) within 1 h.The time-dependent online conversion of ethylene and the ratio of effective catalysts suggested that the effect of water is insignificant in the final growth period of the CNTs compared to that at the beginning.The correlation between the relative activity of the catalyst and the relative density of the CNT agglomerate suggests that the lack of growth volume inside the CNT agglomerate results in a gradual deactivation of the catalyst in the final CNT growth period. Raman characterization suggests that the degree of CNT defects increases with the bulk density of the CNT agglomerates since the mechanical resistance that is exposed on CNTs inside the agglomerate increases with reaction time.Thermal-gravimetric analysis indicates that the purity of CNTs ranges from 95.0%to 99.9%for a product with average purity of 99.2%.The non-uniform purity of the CNTs is due to the difference in mechanical resistance inside and outside the CNT agglomerate.The growth of CNTs outside the agglomerate is nearly free of mechanical resistance compared to that inside the agglomerate and,consequently,results in a high yield and high purity for the CNTs.These results suggest that it is necessary to control the agglomerate size and the structure,and to use a reactor with a large reactor volume for the growth of CNTs with low resistance and with high yield.

Water-Assisted Growth of Carbon Nanotubes over Co/Mo/Al_2O_3 Catalyst

Effect And Mechanism Of Water On Carbon Nanotubes Growth

Growth and Characterization of Bamboo-Like Multiwalled Carbon Nanotubes over Cu/Al2o3 Catalyst

Controlled Growth of Single-Walled Carbon Nanotubes by Catalytic Decomposition of CH4 over Mo/Co/MgO Catalysts

Influence of Cerium Metal As Catalyst on the Growth and Structure of Single-Walled Carbon Nanotubes

Growth Of High-Quality Single-Wall Carbon Nanotubes Without Amorphous Carbon Formation

Effect of organic additives in catalyst preparation on the growth of single-wall carbon nanotubes prepared by catalyst-assisted chemical vapour deposition

CO<sub>2</sub>-Assisted SWNT Growth on Porous Catalysts

A New Understanding of Carbon Nanotube Growth: Activation and Deactivation of a Catalyst

Statistical patterns in high-throughput growth of single-wall carbon nanotubes from Co/Pt/Mo ternary catalysts

Selective growth of semiconducting single-walled carbon nanotubes solely from carbon monoxide

In Situ TEM Observation of the Gasification and Growth of Carbon Nanotubes Using Iron Catalysts

Synthesis Of High Quality Single-Walled Carbon Nanotubes By Cvd And Effect Of Catalyst'S Acidity-Basicity On Nanotubes Growth

Synthesis of Thin-Walled Carbon Nanotubes from Methane by Changing the Ni/Mo Ratio in a Ni/Mo/MgO Catalyst

SiO2-promoted growth of single-walled carbon nanotubes on an alumina supported catalyst

Possible Tactics to Improve the Growth of Single-Walled Carbon Nanotubes by Chemical Vapor Deposition

Controlled Growth of Single-Walled Carbon Nanotubes at Atmospheric Pressure by Catalytic Decomposition of Ethanol and an Efficient Purification Method

Mo-Doped Ni/C Catalyst for Improved Simultaneous Production of Hydrogen and Carbon Nanotubes through Ethanol Decomposition

Combination effect of growth enhancers and carbon sources on synthesis of single-walled carbon nanotubes from solid carbon growth seeds

Carbon fiber-promoted activation of catalyst for efficient growth of single-walled carbon nanotubes

Catalytic co-pyrolysis of waste tea residue and waste plastics to carbon nanomaterials: catalyst support, reaction temperature and product application